Investigation of pitting corrosion damage of a hydraulic press trunk piston

被引：3
|
作者：
Wang, CL [1 ]
Cui, YX
Cui, L
机构：
[1] Harbin Inst Technol, Ctr Anal & Measurement, Harbin 150001, Peoples R China
[2] Harbin Boiler Ltd Corp, Harbin 150001, Peoples R China
来源：
ENGINEERING FAILURE ANALYSIS | 2003年 / 10卷 / 02期
关键词：
corrosion; surface layers; piston; wear; erosion;
D O I：
10.1016/S1350-6307(02)00041-9
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Using metallography, metallurgical analysis, SEM and EDS, a failed hydraulic press trunk piston was analyzed. The result indicates that deficiencies in material composition are the main reasons for the failure. Because of this the piston eroded to form corrosive pits on the surface in service and the pits were developed into hollows and furrows. (C) 2002 Elsevier Science Ltd. All rights reserved.
引用
收藏
页码：251 / 254
页数：4
相关论文
共 50 条
  • [1] Peridynamic modeling of pitting corrosion damage
    Chen, Ziguang
    Bobaru, Florin
    JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 2015, 78 : 352 - 381
  • [2] The Influence of Passive Film Damage on Pitting Corrosion
    Chen, Ziguang
    Zhang, Guangfeng
    Bobaru, Florin
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2016, 163 (02) : C19 - C24
  • [3] Corrosion model captures dynamics of pitting damage
    Bobaru, Florin
    MATERIALS PERFORMANCE, 2015, 54 (05) : 17 - 19
  • [4] An Estimate of the Damage to the Blade Surface by Pitting Corrosion
    Sokolov, V.S.
    Lebedeva, A.I.
    Nogin, V.I.
    Thermal Engineering, 1998, 45 (08): : 665 - 667
  • [5] Investigation of the Nature of Pitting Corrosion of Gold Coins
    Syrnev, B.V.
    Tuganbaev, F.S.
    Sadibekov, A.B.
    Ivashchenko, E.N.
    Kulenova, N.A.
    Sadenova, M.A.
    Seraya, N.V.
    Russian Journal of Non-Ferrous Metals, 2024, 65 (03) : 170 - 177
  • [6] Numerical investigation of pitting corrosion in clinched joints
    Harzheim, Sven
    Chen, Chin
    Hollmer, Katharina
    Hofmann, Martin
    Zimmermann, Martina
    Wallmersperger, Thomas
    ACTA MECHANICA, 2025,
  • [7] Investigation of pitting corrosion by potentiostatic polarization measurements
    Loukaycheva, M. H.
    BULGARIAN CHEMICAL COMMUNICATIONS, 2016, 48 : 115 - 118
  • [8] AN INVESTIGATION OF THE TOLERANCE OF RISER FATIGUE TO CORROSION PITTING
    Urthaler, Yetzirah
    Cerkovnik, Mark
    Yin, Fengjie
    Saldana, David
    Gordon, Robin
    PROCEEDINGS OF THE ASME 32ND INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING - 2013, VOL 4B, 2013,
  • [9] Theory for the deterministic prediction of pitting corrosion damage on aluminum
    Macdonald, DD
    Engelhardt, G
    CORROSION AND PROTECTION OF LIGHT METAL ALLOYS, 2004, 2003 (23): : 316 - 343
  • [10] Characterization of pitting corrosion damage through multiscale analysis
    Frantziskonis, GN
    Simon, LB
    Woo, J
    Matikas, TE
    NONDESTRUCTIVE EVALUATION OF AGING MATERIALS AND COMPOSITES III, 1999, 3585 : 48 - 58
12345