Effect of carbon deposits on the corrosion behavior of anodized 2214 T6 aluminium alloy

被引：0
|
作者：
Snogan, F [1 ]
Blanc, C [1 ]
Pébère, N [1 ]
Le Pottier, N [1 ]
Viola, A [1 ]
Mankowski, G [1 ]
机构：
[1] ENSIACET, CNRS, UMR 5085, Ctr Interuniv Rech & Ingn Mat, F-31077 Toulouse 4, France
来源：
CORROSION AND CORROSION PROTECTION | 2001年 / 2001卷 / 22期
关键词：
D O I：
暂无
中图分类号：
O646 [电化学、电解、磁化学];
学科分类号：
081704 ;
摘要：
The influence of carbon deposits on sealed porous anodic films formed on aluminium in a sulphuric acid electrolyte has been studied using optical microscopy and electrochemical impedance spectroscopy. No influence of carbon can be observed on intact films. In the case where films present defects, carbon has an accelerating effect on the degradation of the sealed layers. It has been shown that temperature is a possible factor for creating defects such as cracks.
引用
收藏
页码：1026 / 1031
页数：6
相关论文
共 50 条
  • [31] Wear and corrosion performance of two different tempers (T6 and T73) of AA7075 aluminium alloy after nitrogen implantation
    Abreu, C. M.
    Cristobal, M. J.
    Figueroa, R.
    Pena, G.
    APPLIED SURFACE SCIENCE, 2015, 327 : 51 - 61
  • [32] Effect of Welding Parameters on the Corrosion Behavior of Dissimilar Alloy Welds of T6 AA6061 Al-Galvanized Mild Steel
    Sravanthi, S. S.
    Acharyya, Swati Ghosh
    Prabhakar, K. V. Phani
    Padmanabham, G.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2018, 27 (10) : 5518 - 5531
  • [33] Combined Corrosion and Wear of Aluminium Alloy 7075-T6
    Liu Y.
    Mol J.M.C.
    Janssen G.C.A.M.
    Journal of Bio- and Tribo-Corrosion, 2016, 2 (2)
  • [34] Fatigue behavior of crossing MIG and friction stir welds in aluminium 6082 T6
    Kosteas, D
    Radbeck, C
    ADVANCES IN STRUCTURES, VOLS 1 AND 2, 2003, : 449 - 452
  • [35] WEAR MECHANISMS OF DIAMOND-LIKE CARBON COATED TOOLS IN TAPPING OF AA6351 T6 ALUMINIUM ALLOY
    Fernandes, Gustavo H. N.
    Lopes, Guilherme H. F.
    Barbosa, Lucas M. Q.
    Martins, Paulo S.
    Machado, Alisson R.
    49TH SME NORTH AMERICAN MANUFACTURING RESEARCH CONFERENCE (NAMRC 49, 2021), 2021, 53 : 293 - 298
  • [36] Characterization of sealed anodic layers on 7050 T74 and 2214 T6 aluminum alloys
    Snogan, F
    Blanc, C
    Mankowski, G
    Pébère, N
    CORROSION AND CORROSION PROTECTION, 2001, 2001 (22): : 138 - 145
  • [37] THE EFFECTS OF T4 AND T6 HEAT TREATMENT ON THE CORROSION BEHAVIOR OF MGZNCA ALLOYS
    Smith, Christopher
    Xu, Zhigang
    Sankar, Jagannathan
    INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION - 2012, VOL 3, PTS A-C: DESIGN, MATERIALS, AND MANUFACTURING, 2013, : 745 - 759
  • [38] Exfoliation corrosion behavior of T6 treated 2090 Al-Li alloy in EXCO solution, and EIS during exfoliation corrosion evolution
    Su, JX
    Zhang, Z
    Cao, FH
    Zhang, JQ
    Cao, CN
    ACTA METALLURGICA SINICA, 2005, 41 (09) : 974 - 978
  • [39] Analysis of strain rate behavior of an A1 6061 T6 alloy
    Manes, A.
    Peroni, L.
    Scapin, M.
    Giglio, M.
    11TH INTERNATIONAL CONFERENCE ON THE MECHANICAL BEHAVIOR OF MATERIALS (ICM11), 2011, 10 : 3477 - 3482
  • [40] Small fatigue crack growth in aluminium alloy EN-AW 6082/T6
    Jisa, D.
    Liskutin, P.
    Kruml, T.
    Polak, J.
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (12) : 1913 - 1920
12345