In-situ TEM observation of silver nanocrystals in an Ag-implanted SiO2 film

被引：11
|
作者：
Jiang, CZ [1 ]
Fan, XJ [1 ]
机构：
[1] Wuhan Univ, Dept Phys, Wuhan 430072, Peoples R China
来源：
SURFACE & COATINGS TECHNOLOGY | 2000年 / 131卷 / 1-3期
关键词：
in-situ; silver nanocrystal; TEM observation;
D O I：
10.1016/S0257-8972(00)00802-1
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The Ag ions were implanted in an amorphous SiO2 film, which was placed in a sample chamber of TEM. The concentration and size distribution of the Ag nanocrystals as functions of both the ion dose and the annealing temperature were examined in-situ by using this TEM. The selected diffraction pattern determined the Ag nanocrystal's presence and the dark field micrograph showed the shape and the concentration of the Ag nanocrystals. The implantation results demonstrated an average size diminution and a significant concentration increase of the Ag nanocrystals when the dose increased. The annealing results showed a loss of silver at 300 degreesC and above. (C) 2000 Elsevier Science B.V. All rights reserved.
引用
收藏
页码：330 / 333
页数：4
相关论文
共 50 条
  • [31] Sintering behavior of SiO2 aerogel composites reinforced by mullite fibers via in-situ rapid heating TEM observations
    Cai, Huafei
    Jiang, Yonggang
    Chen, Qu
    Zhang, Sizhao
    Li, Liangjun
    Feng, Junzong
    Feng, Jian
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2020, 40 (01) : 127 - 135
  • [32] XPS and in-situ IR investigation of Ru/SiO2 catalyst
    Sayan, S
    Suzer, S
    Uner, DO
    JOURNAL OF MOLECULAR STRUCTURE, 1997, 410 : 111 - 114
  • [33] Influence of Radiation on the Luminescence of Silicon Nanocrystals Embedded into SiO2 Film
    Lisovskyy, I. P.
    Voitovych, M. V.
    Voitovych, V. V.
    Khacevich, I. M.
    JOURNAL OF NANOMATERIALS, 2016, 2016
  • [34] Ostwald ripening in a Pt/SiO2 model catalyst studied by in situ TEM
    Simonsen, Soren Bredmose
    Chorkendorff, Ib
    Dahl, Soren
    Skoglundh, Magnus
    Sehested, Jens
    Helveg, Stig
    JOURNAL OF CATALYSIS, 2011, 281 (01) : 147 - 155
  • [35] COLLOID FORMATION EFFECTS ON DEPTH PROFILE OF IMPLANTED AG IN SIO2 GLASS
    MATSUNAMI, N
    HOSONO, H
    APPLIED PHYSICS LETTERS, 1993, 63 (15) : 2050 - 2052
  • [36] Antibacterial activity of silver ions implanted in SiO2 filler on oral streptococci
    Yamamoto, K
    Ohashi, S
    Aono, M
    Kokubo, T
    Yamada, I
    Yamauchi, J
    DENTAL MATERIALS, 1996, 12 (04) : 227 - 229
  • [37] Optical properties of Si-doped GaN nanocrystals in SiO2/GaN/SiO2 thin film structure
    Das, S. N.
    Bhattacharyya, S. R.
    Gayen, R. N.
    Pal, A. K.
    JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2009, 42 (13)
  • [38] Depth distribution of luminescent Si nanocrystals in Si implanted SiO2 films on Si
    Brongersma, M.L.
    Polman, A.
    Min, K.S.
    Atwater, H.A.
    Journal of Applied Physics, 86 (02):
  • [39] Depth distribution of luminescent Si nanocrystals in Si implanted SiO2 films on Si
    Brongersma, ML
    Polman, A
    Min, KS
    Atwater, HA
    JOURNAL OF APPLIED PHYSICS, 1999, 86 (02) : 759 - 763
  • [40] In-situ high resolution transmission electron microscopy observation of silicon nanocrystal nucleation in a SiO2 bilayered matrix
    Yang, T. C. -J.
    Kauffmann, Y.
    Wu, L.
    Lin, Z.
    Jia, X.
    Puthen-Veettil, B.
    Zhang, T.
    Conibeer, G.
    Perez-Wurfl, I.
    Rothschild, A.
    APPLIED PHYSICS LETTERS, 2014, 105 (05)
12345