Effect of Boron Micro-alloying on Microstructure and Corrosion Behavior of Dual-Phase Steel

被引：10
|
作者：
Kumar, Satendra [1 ]
Desai, Rahul [1 ]
机构：
[1] JSW Steel Ltd, R&D & SS Dept, Vijayanagar Works, Bellary 583275, Karnataka, India
来源：
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE | 2019年 / 28卷 / 10期
关键词：
boron micro-alloying; corrosion; dual-phase steel; martensite; mechanical properties;
D O I：
10.1007/s11665-019-04364-w
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The present work aims to understand the effect of boron (B) as a micro-alloying element on the mechanical properties and corrosion behavior of a dual-phase steel that was prepared from boron-added steel via hot rolling. The 'B' micro-alloying increased the volume fraction of martensite from similar to 25 to 50% and improved the hardenability as compared to unalloyed DP steel subjected to similar rolling and heat treatment conditions. The yield strength, tensile strength and corrosion resistance of boron-added DP steel significantly improved from 405 to 690 MPa, 632 to 890 MPa and 0.125 to 0.110 mm/year, respectively, as compared to the unalloyed DP steel.
引用
收藏
页码：6228 / 6236
页数：9
相关论文
共 50 条
  • [41] Micro-alloying of Rare Earths in Heavy Rail Steel
    Huang Yahe
    Liu Chengjun
    Jiang Maofa
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 : 245 - 249
  • [42] BAUSCHINGER EFFECT IN A DUAL-PHASE STEEL
    GOEL, A
    RAY, RK
    MURTY, GS
    SCRIPTA METALLURGICA, 1983, 17 (03): : 375 - 380
  • [43] Effect of Microstructure on Corrosion Fatigue Behavior of 1500 MPa Level Carbide-Free Bainite/Martensite Dual-Phase High Strength Steel
    Lei Xu
    Dong-yuan Wei
    Yang Yu
    Han Zhang
    Bing-zhe Bai
    Journal of Iron and Steel Research International, 2011, 18 : 63 - 67
  • [44] Relationship between Microstructure and Corrosion Behavior in Dual-Phase Steels with Various Si Content
    Nouri, Ashkan
    Hassannejad, Hossein
    Farrokhi-Rad, Morteza
    STEEL RESEARCH INTERNATIONAL, 2019, 90 (11)
  • [45] Effect of Microstructure on Corrosion Fatigue Behavior of 1500 MPa Level Carbide-Free Bainite/Martensite Dual-Phase High Strength Steel
    Xu Lei
    Wei Dong-yuan
    Yu Yang
    Zhang Han
    Bai Bing-zhe
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2011, 18 (04) : 63 - 67
  • [46] Effect of Microstructure on Corrosion Fatigue Behavior of 1500 MPa Level Carbide-Free Bainite/Martensite Dual-Phase High Strength Steel
    XU Lei
    JournalofIronandSteelResearch(International), 2011, 18 (04) : 63 - 67
  • [47] THE EFFECT OF PHASE CONTINUITY ON THE FATIGUE AND CRACK CLOSURE BEHAVIOR OF A DUAL-PHASE STEEL
    RAMAGE, RM
    JATA, KV
    SHIFLET, GJ
    STARKE, EA
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1987, 18 (07): : 1291 - 1298
  • [48] CORROSION PERFORMANCE OF DUAL-PHASE STEEL EMBEDDED IN CONCRETE
    Ismail, Mohammad
    Hamzah, Esah
    Guan, Goh Chun
    Rahman, Ihsan Abd
    ARABIAN JOURNAL FOR SCIENCE AND ENGINEERING, 2010, 35 (2B): : 81 - 90
  • [49] IMPROVING QUALITY OF TUBE STEEL BY MICRO-ALLOYING WITH TITANIUM
    YAKUBOVICH, YV
    FURMAN, YS
    IVANOV, GM
    GOLDINOV, AY
    MAMYCHEVA, LP
    STEEL IN THE USSR, 1976, 6 (10): : 555 - 557
  • [50] Characterization of a Continuously Cooled Dual-Phase Steel Microstructure
    F. Farias
    M. Balbi
    M. N. Batista
    I. Alvarez-Armas
    Metallurgical and Materials Transactions A, 2018, 49 : 6010 - 6021
12345