Microstructural evolution of thermal barrier coatings during isothermal oxidation

被引：3
|
作者：
Salazar, A. [1 ]
Gomez-Garcia, J. [1 ]
Poza, P. [1 ]
Utrilla, V. [1 ]
机构：
[1] Univ Rey Juan Carlos, Dept Ciencia & Ingn Mat, ESCET, C-Tulipan S-N, Madrid 28933, Spain
来源：
LAYERED, FUNCTIONAL GRADIENT CERAMICS, AND THERMAL BARRIER COATINGS: DESIGN, FABRICATION AND APPLICATIONS | 2007年 / 333卷
关键词：
thermal barrier coatings; thermal spray; oxidation; heat treatment; scanning electron microscopy; transmission electron microscopy; X ray diffraction;
D O I：
10.4028/www.scientific.net/KEM.333.269
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
This paper analyses the degradation of a ceramic top coating 70%ZrO2 - 30%CaO deposited onto a stainless steel AISI 304 by thermal spray, using Ni-6%Al-5%Mo as overlay coating. These thermal barrier coatings were heat treated for 48, 120 and 288 h at 800 degrees C to evaluate the degradation of these materials by isothermal oxidation. The microstructure evolution during oxidation was analysed by environmental scanning electron microscopy, transmission electron microscopy and X ray microanalysis. A thermally grown oxide layer was observed between the overlay coating and the ceramic top coating after oxidation. This layer was formed by a mixed Al, Ni and Mo oxides.
引用
收藏
页码：269 / +
页数：2
相关论文
共 50 条
  • [1] Microstructural evolution at interfaces of thermal barrier coatings during isothermal oxidation
    Liu, Y. Z.
    Zheng, S. J.
    Zhu, Y. L.
    Wei, H.
    Ma, X. L.
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2016, 36 (07) : 1765 - 1774
  • [2] Damage evolution and stress analysis in zirconia thermal barrier coatings during cyclic and isothermal oxidation
    Singh, JP
    Nair, BG
    Renusch, DP
    Sutaria, MP
    Grimsditch, MH
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2001, 84 (10) : 2385 - 2393
  • [3] An investigation of the effects of isothermal exposure on microstructural evolution and oxidation in a thermal barrier coating
    Chang, T
    Mercer, C
    Walter, M
    Soboyejo, WO
    DURABLE SURFACES, 2001, 197 : 185 - 198
  • [4] Investigation of Microstructural Properties and Isothermal Oxidation Behavior of Thermal Barrier Coatings (TBCs) with MCrAlY Bond Coat
    Ozkan, Dervis
    JOURNAL OF POLYTECHNIC-POLITEKNIK DERGISI, 2022, 25 (01): : 331 - 338
  • [5] Evaluation of microstructural evolution in thermal barrier coatings during thermal cycling using impedance spectroscopy
    Song, SH
    Xiao, P
    Weng, LQ
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2005, 25 (07) : 1167 - 1173
  • [6] Microstructural evolution and degradation modes in cyclic and isothermal oxidation of an EB-PVD thermal barrier coating
    Ibegazene-Ouali, F
    Mevrel, R
    Rio, C
    Renollet, Y
    MATERIALS AT HIGH TEMPERATURES, 2000, 17 (02) : 205 - 217
  • [7] Damage evolution and lifetime prediction of thermal barrier coatings during cyclic oxidation
    Beck, Tilmann
    Herzog, Roland
    Trunova, Olena
    Steinbrech, Rolf W.
    Singheiser, Lorenz
    PLASTICITY, FAILURE AND FATIGUE IN STRUCTURAL MATERIALS-FROM MACRO TO NANO: PROCEEDINGS OF THE HAEL MUGHRABI HONORARY SYMPOSIUM, 2008, : 207 - 212
  • [8] Segregation and microstructural evolution at interfaces of atmospheric plasma sprayed thermal barrier coatings during thermal cycling
    Liu, Y. Z.
    Hu, X. B.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 819
  • [9] Effects of isothermal oxidation on microstructure and mechanical properties of thermal barrier coatings
    Liu, Y. Z.
    Hu, X. B.
    Zhu, Y. L.
    Wei, H.
    Dravid, Vinayak P.
    Zhang, W. W.
    CERAMICS INTERNATIONAL, 2019, 45 (07) : 8815 - 8823
  • [10] Interfacial degradation of thermal barrier coatings in isothermal and cyclic oxidation tests
    Jeon, Seol
    Lee, Heesoo
    Choi, Youngkue
    Shin, Hyun-Gyoo
    Jeong, Young-Keun
    JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY, 2014, 24 (04): : 151 - 157
12345