The Relationship between Microstructure and Fracture Behavior of TiAl/Ti2AlNb SPDB Joint with High Temperature Titanium Alloy Interlayers

被引:2
|
作者
Liao, Minxing [1 ]
Tian, Hao [1 ]
Zhao, Lei [2 ]
Zhang, Boxian [3 ]
He, Jianchao [1 ]
机构
[1] Harbin Inst Technol, Inst Special Environm Phys Sci, Shenzhen 518055, Peoples R China
[2] Cent Iron & Steel Res Inst, Dept Funct Mat Res, Beijing 100081, Peoples R China
[3] AVIC Mfg Technol Inst, Aeronaut Key Lab Welding & Joining Technol, Beijing 100024, Peoples R China
基金
中国国家自然科学基金;
关键词
spark plasma diffusion bonding; TiAl; microstructure; mechanical properties; fracture; GAMMA-TIAL ALLOYS; MECHANICAL-PROPERTIES; PURE TI; DEFORMATION; EVOLUTION; PHASE; FOIL; NB;
D O I
10.3390/ma15144849
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In this paper, spark plasma diffusion bonding technology was employed to join TiAl and Ti2AlNb with high temperature titanium alloy interlayer at 950 degrees C/10kN/60 min, then following furnace cooling at cooling rate up to 100 degrees C/min. After welding, the joint was aging heat-treated at 800 degrees C for 24 h. The microstructure and the elements diffusion of the TiAl/Ti2AlNb joint was analyzed by field emission scanning electron microscopy (FESEM) with EDS. Moreover, the tensile properties of the joint were tested at room temperature, 650 degrees C, and 750 degrees C. The results show that the spark plasma diffusion bonding formed a high quality TiAl/Ti2AlNb joint without microcracks or microvoids, while also effectively protecting the base metal. Significant differences in the microstructure of the joint appeared from TiAl side to Ti2AlNb side: TiAl BM (Base Metal) -> DP(Duplex) and NG (Near-Gamma) -> alpha(2)-phase matrix with needle-like alpha-phase -> bulk alpha(2)-phase -> needle-like alpha-phase -> metastable beta-phase -> Ti2AlNb BM. After heat treatment at 800 degrees C for 24 h, the microstructure of the TiAl side and the interlayer region did not change, but the density and size of the needle-like alpha-phase in region 3 increased slightly. The microstructure of Ti2AlNb near the weld changed obviously, and a large number of fine O phases are precipitated from the metastable beta phase matrix after heat treatment. Except for the Ti2AlN near-interface region, the effect of heat treatment on the microstructure of the joint is not significant. The microhardness of the joint is in the shape of a mountain peak. The maximum microhardness at the interface is above 500 HV, and it is significantly reduced to 400 HV after heat treatment. The fracture of the joint occurred at the interface at room temperature, 650 degrees C, and 750 degrees C. with the tensile strength 450 MPa, 540 MPa, and 471 Mpa, respectively, and mainly showing brittle fracture.
引用
收藏
页数:14
相关论文
共 50 条
  • [21] Microstructure and properties of pulse current promoted diffusion welding TiAl/Ti2AlNb joint with Ti69NbCrZrX interlayer
    Lyu Yanlong
    Fan Jiafeng
    Hou Jinbao
    Chai Lu
    Tao Jun
    CAILIAO GONGCHENG-JOURNAL OF MATERIALS ENGINEERING, 2024, 52 (12): : 143 - 150
  • [22] Investigation of interfacial microstructure and mechanical performance within TiAl to Ti2AlNb alloy vacuum diffusion bonded joints
    Huang, Libing
    Lu, Yaxin
    Li, Jiachen
    Li, Chao
    Li, Peng
    Zhao, Dongsheng
    Shi, Shuyan
    Liu, Xiaoying
    Ma, Xiong
    Dong, Honggang
    INTERMETALLICS, 2024, 174
  • [23] Tribological Behavior of Ti2AlNb Alloy by Surface plasmas Carburized
    Zhu, Dan Yang
    Liang, Wen Ping
    Miao, Qiang
    Guo, Kai
    Li, Long
    ADVANCED COMPOSITE MATERIALS, PTS 1-3, 2012, 482-484 : 914 - 918
  • [24] Thermal deformation behavior and mechanism of intermetallic alloy Ti2AlNb
    Zhang, Qin-chai
    Chen, Ming-he
    Wang, Hui
    Wang, Ning
    Ouyang, Jin-dong
    Li, Xin-xiao
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2016, 26 (03) : 722 - 728
  • [25] Microstructure evolution and mechanical properties of Ti2AlNb/TiAl brazed joint using newly-developed Ti-Ni-Nb-Zr filler alloy
    Ren, Xinyu
    Ren, Haishui
    Shang, Yonglai
    Xiong, Huaping
    Zhang, Kai
    Zheng, Jinghua
    Liu, Dong
    Lin, Jianguo
    Jiang, Jun
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2020, 30 (03) : 410 - 416
  • [26] Microstructure and property of Ti2AlNb alloy by selective electron beam melting
    Che Q.
    He W.
    Li H.
    Cheng K.
    Wang Y.
    Cailiao Gongcheng/Journal of Materials Engineering, 2022, 50 (07): : 156 - 164
  • [27] Microstructure and mechanical properties of nanostructured intermetallic alloy based on Ti2AlNb
    Shagiev, M. R.
    Salishchev, G. A.
    NANOMATERIALS BY SEVERE PLASTIC DEFORMATION IV, PTS 1 AND 2, 2008, 584-586 : 153 - 158
  • [28] The Effect of Coatings on the Oxidation Kinetics of Intermetallic Titanium Alloys of the Ti2AlNb and γ-TiAl Systems
    Skvortsova, S., V
    Zolotareva, A. Yu
    PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, 2020, 56 (07) : 1232 - 1238
  • [29] The Effect of Coatings on the Oxidation Kinetics of Intermetallic Titanium Alloys of the Ti2AlNb and γ-TiAl Systems
    S. V. Skvortsova
    A. Yu. Zolotareva
    Protection of Metals and Physical Chemistry of Surfaces, 2020, 56 : 1232 - 1238
  • [30] Effect of processing parameters on the microstructure and mechanical properties of TiAl/Ti2AlNb laminated composites
    Donghai Li
    Binbin Wang
    Liangshun Luo
    Xuewen Li
    Yanjin Xu
    BinQiang Li
    Diween Hawezy
    Liang Wang
    Yanqing Su
    Jingjie Guo
    Hengzhi Fu
    JournalofMaterialsScience&Technology, 2022, 109 (14) : 228 - 244