Structural, magnetic, and transport properties of Fe1-xRhx/MgO(001) films grown by molecular-beam epitaxy

Fe1-xRhx layers are grown with varying rhodium fraction x on (001)-oriented MgO substrates by molecular-beam epitaxy. Film structural, morphological, magnetic, and transport properties are investigated. At room temperature, layers are ferromagnetic (FM) for x< 0.48 and antiferromagnetic (AF) for x> 0.48. Separating the two magnetically ordered phases at x = 0.48 is an abrupt change in the Fe1-xRhx lattice parameter of Delta a = 0.0028 nm (Delta a/a = -0.9%). For AF layers, the FM state is recovered by heating across a first-order phase transition. The transition leads to a large resistivity modulation, Delta rho/rho = 80%, over a narrow temperature range, Delta T = 3K, in stoichiometric Fe0.50Rh0.50/MgO(001). For samples with compositions deviating from x = 0.50, fluctuations broaden DT and defect scattering reduces Delta rho/rho. Published by AIP Publishing.