Intermetallic morphology and damage evolution under thermomechanical fatigue of lead (Pb)-free solder interconnections

被引：41
|
作者：
Dunford, S [1 ]
Canumalla, S [1 ]
Viswanadham, P [1 ]
机构：
[1] Nokia, Irving, TX 75039 USA
来源：
54TH ELECTRONIC COMPONENTS & TECHNOLOGY CONFERENCE, VOLS 1 AND 2, PROCEEDINGS | 2004年
关键词：
D O I：
10.1109/ECTC.2004.1319418
中图分类号：
TM [电工技术]; TN [电子技术、通信技术];
学科分类号：
0808 ; 0809 ;
摘要：
The variety and complexity of intermetallic morphologies are highlighted in this paper along with their role in defining failure under thermal fatigue. Some of the failure mechanisms for Sn3.8Ag0.7Cu and Sn3.5Ag solder on organic solderability preservative (OSP) and electroless Ni immersion Au (ENIG) pad surface finishes are discussed. Interrupted fatigue test results were used to document the location and progression of damage.
引用
收藏
页码：726 / 736
页数：11
相关论文
共 50 条
  • [31] Localized recrystallization and cracking of lead-free solder interconnections under thermal cycling–ERRATUM
    Hongtao Chen
    Maik Mueller
    Toni Tuomas Mattila
    Jue Li
    Xuwen Liu
    Klaus-Juergen Wolter
    Mervi Paulasto-Kröckel
    Journal of Materials Research, 2012, 27 : 978 - 978
  • [32] Localized Recrystallization and Cracking Behavior of Lead-free Solder Interconnections under Thermal Cycling
    Chen, H. T.
    Mattila, T.
    Li, J.
    Liu, X. W.
    Li, M. Y.
    Kivilahti, J. K.
    2009 INTERNATIONAL CONFERENCE ON ELECTRONIC PACKAGING TECHNOLOGY & HIGH DENSITY PACKAGING (ICEPT-HDP 2009), 2009, : 486 - +
  • [33] Creep and fatigue behaviors of the lead-free Sn–Ag–Cu–Bi and Sn60Pb40 solder interconnections at elevated temperatures
    X. P. Zhang
    C. B. Yu
    S. Shrestha
    L. Dorn
    Journal of Materials Science: Materials in Electronics, 2007, 18 : 665 - 670
  • [34] Failure behavior of small outline J lead/Sn-X (X = AgCu or Pb) solder joints under thermomechanical fatigue test
    Wu, PL
    Huang, MK
    Lee, C
    Tzan, SR
    MATERIALS CHEMISTRY AND PHYSICS, 2004, 87 (2-3) : 285 - 291
  • [35] Evaluation of Thermomechanical Fatigue Lifetime of BGA Lead-Free Solder Joints and Impact of Isothermal Aging
    Roumanille, Pierre
    Ben Romdhane, Emna
    Pin, Samuel
    Nguyen, Patrick
    Deletage, Jean-Yves
    Guedon-Gracia, Alexandrine
    Fremont, Helene
    2022 IEEE INTERNATIONAL RELIABILITY PHYSICS SYMPOSIUM (IRPS), 2022,
  • [36] Evaluation of thermomechanical fatigue lifetime of BGA lead-free solder joints and impact of isothermal aging
    Roumanille, Pierre
    Ben Romdhane, Emna
    Pin, Samuel
    Nguyen, Patrick
    Deletage, Jean-Yves
    Guedon-Gracia, Alexandrine
    Fremont, Helene
    MICROELECTRONICS RELIABILITY, 2021, 126
  • [37] FATIGUE BEHAVIOUR OF LEAD-FREE SOLDER INTERCONNECTIONS IN LIFE PREDICTION OF TRILAYER STRUCTURES SUBJECTED TO THERMAL CYCLING
    Shirazi, Alireza
    Lu, Hua
    Varvani-Farahani, Ahmad
    PROCEEDINGS OF THE ASME 10TH INTERNATIONAL MANUFACTURING SCIENCE AND ENGINEERING CONFERENCE, 2015, VOL 1, 2015,
  • [38] Effects of Microstructure Evolution on Damage Accumulation in Lead-Free Solder Joints
    Yang, Linlin
    Yin, Liang
    Roggeman, Brian
    Borgesen, Peter
    2010 PROCEEDINGS 60TH ELECTRONIC COMPONENTS AND TECHNOLOGY CONFERENCE (ECTC), 2010, : 1518 - 1523
  • [39] Effect of Isothermal Aging and Electromigration on the Microstructural Evolution of Solder Interconnections During Thermomechanical Loading
    T. Laurila
    J. Karppinen
    V. Vuorinen
    J. Li
    A. Paul
    M. Paulasto-Kröckel
    Journal of Electronic Materials, 2012, 41 : 3179 - 3195
  • [40] Thermomechanical reliability of lead free solder joint in SMT assembly
    Sandera, J.
    2007 30TH INTERNATIONAL SPRING SEMINAR ON ELECTRONICS TECHNOLOGY, 2007, : 123 - 127
12345