Microstructural analysis and corrosion behaviour of D9 stainless steel - Zirconium metal waste form alloys

被引：31
|
作者：
Bairi, Lipika Rani [1 ]
Ningshen, S. [1 ]
Mudali, U. Kamachi [1 ]
Raj, Baldev [1 ]
机构：
[1] Indira Gandhi Ctr Atom Res, Corros Sci & Technol Div, Kalpakkam 603102, Tamil Nadu, India
来源：
CORROSION SCIENCE | 2010年 / 52卷 / 07期
关键词：
Stainless steel; Zirconium; Intermetallics; SEM; XRD; EIS; PHASES; MANAGEMENT;
D O I：
10.1016/j.corsci.2010.03.018
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Metal waste form (MWF) alloys of D9 stainless steel with 5-20 wt.% zirconium (Zr) were cast and used for the present work. The microstructural analysis by scanning electron microscopy of as-cast MWF alloys showed the presence of two distinctly different phases. Phases identified by X-ray diffraction techniques are mostly iron-based gamma-austenite, Fe-Zr and Ni-Zr-type intermetallics. Corrosion properties evaluated by potentiodynamic polarization method in de-mineralized water at pH 1, 5, and 8 showed lower breakdown potential at pH 1 compared to pH 5 and 8. Impedance study showed a single semicircle curve with high polarization resistance indicating stable passive film under all conditions. (C) 2010 Elsevier Ltd. All rights reserved.
引用
收藏
页码：2291 / 2302
页数：12
相关论文
共 50 条
  • [41] Corrosion of stainless steel valves in a reverse osmosis system: Analysis of corrosion products and metal loss
    Xu, Xiyan
    Liu, Shuming
    Liu, Ying
    Smith, Kate
    Cui, Yong
    ENGINEERING FAILURE ANALYSIS, 2019, 105 : 40 - 51
  • [42] Application of thin layer activation technique to study surface erosion of D9 stainless steel during laser ablation process
    Datta, J.
    Dasgupta, S.
    Verma, R.
    Chowdhury, D. P.
    Sugathan, Bijoy
    Nilaya, J. P.
    Biswas, D. J.
    JOURNAL OF RADIOANALYTICAL AND NUCLEAR CHEMISTRY, 2016, 308 (01) : 329 - 334
  • [43] Application of thin layer activation technique to study surface erosion of D9 stainless steel during laser ablation process
    J. Datta
    S. Dasgupta
    R. Verma
    D. P. Chowdhury
    Bijoy Sugathan
    J. P. Nilaya
    D. J. Biswas
    Journal of Radioanalytical and Nuclear Chemistry, 2016, 308 : 329 - 334
  • [44] Microstructural characterisation of a dissimilar weld of alloy D9 and AISI 316M stainless steel produced using a 2.5kW CW CO2 laser
    Kaul, R
    Ganesh, P
    Ittoop, MO
    Nath, AK
    Kumar, A
    Bhatt, RB
    Kumar, A
    LASERS IN ENGINEERING, 2002, 12 (02) : 117 - 133
  • [45] Corrosion interactions between stainless steel and lead vanado-iodoapatite nuclear waste form part II
    Yao, Tiankai
    Guo, Xiaolei
    Lei, Penghui
    Wang, Yachun
    Frankel, Gerald S.
    Lian, Jie
    NPJ MATERIALS DEGRADATION, 2020, 4 (01)
  • [46] Corrosion interactions between stainless steel and lead vanado-iodoapatite nuclear waste form part II
    Tiankai Yao
    Xiaolei Guo
    Penghui Lei
    Yachun Wang
    Gerald S. Frankel
    Jie Lian
    npj Materials Degradation, 4
  • [47] Microstructural effects on the short crack behaviour of a stainless steel weld metal during low-cycle fatigue
    Zhao, YX
    Gao, Q
    Wang, JN
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1999, 22 (06) : 469 - 480
  • [48] Microstructural effects on the short crack behaviour of a stainless steel weld metal during low-cycle fatigue
    Zhao, Y.-X.
    Gao, Q.
    Wang, J.-N.
    Fatigue and Fracture of Engineering Materials and Structures, 1999, 22 (06): : 469 - 480
  • [49] IMPROVED CORROSION-RESISTANCE ON REFRACTORY-METAL STABILIZED AMORPHOUS STAINLESS-STEEL ALLOYS
    WANG, R
    JOURNAL OF METALS, 1980, 32 (08): : 66 - 66
  • [50] STRUCTURE AND CORROSION BEHAVIOUR OF NANOCRYSTALLINE COBALT-MOLYBDENUM ALLOYS ELECTRODEPOSITED ON 316L STAINLESS STEEL
    Latkiewicz, Michal
    Krawiec, Halina
    Vignal, Vincent
    Erazmus-Vignal, Paulina
    ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 2015, 39 (3-4): : 167 - 174
12345