A deep-sea corrosion study on titanium and Ti6A14V alloy

被引：0

作者：

Venkatesan, R ^{[1
]}

Dwarakadasa, ES

Ravindran, M

机构：

[1] Natl Inst Ocean Technol, Madras, Tamil Nadu, India

[2] Indian Inst Sci, Dept Met, Bangalore 560012, Karnataka, India

来源：

CORROSION PREVENTION & CONTROL | 2004年 / 51卷 / 03期

关键词：

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

THE CORROSION behaviour of titanium and titanium alloy Ti-6Al-4V in a deep-sea environment the Indian Ocean is presented. For the first time, coupons of these materials were exposed for longer duration at great depth in the ocean. Weight-loss measurements did not show any corrosion of the titanium or the alloy at depths of 500, 1200, 3500, and 5100m. Tensile tests were carried out on the deep-sea exposed specimens, and were compared with unexposed control specimens. The results show that the tensile strength did not change after deep-sea exposure.

引用

页码：98 / 103

页数：6

共 50 条

[31] Structural characterization of titanium oxide layers prepared by plasma based ion implantation with oxygen on Ti6A14V alloy
Li, Jinlong
Sun, Mingren
Ma, Xinxin
APPLIED SURFACE SCIENCE, 2006, 252 (20) : 7503 - 7508
[32] Corrosion rate of sand blasted and acid etched Ti6A14V for dental implants
Strnad, Gabriela
Chirila, Nicolae
8TH INTERNATIONAL CONFERENCE INTERDISCIPLINARITY IN ENGINEERING, INTER-ENG 2014, 2015, 19 : 909 - 915
[33] FRICTION AND WEAR BEHAVIORS OF Ti6A14V ALLOY TREATED BY PLASMA Ni ALLOYING
Wang, Zhenxia
Cai, Wenlan
Wu, Hairui
Lin, Naiming
Yao, Xiaohong
He, Zhiyong
Liu, Xiaoping
SURFACE REVIEW AND LETTERS, 2018, 25 (05)
[34] MODELING OF DYNAMIC RECRYSTALLIZATION OF Ti6A14V ALLOY USING A CELLULAR AUTOMATON APPROACH
J.W.Zhao~(1)*) H.Din~(1)) W.J.Zhao~(1)) F.R.Cao~(1)) H.L.Hou~(2)) Z.Q.Li~(2)) 1)School of Materials and Metallurgy
Acta Metallurgica Sinica(English Letters), 2008, (04) : 260 - 268
[35] Bacteria adherence property of molybdenum nitride modified layer on Ti6A14V alloy
Fan Ai-lan
Tian Lin-hai
Qin Lin
Tang Bin
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2007, 17 : S889 - S891
[36] Nanoindentation Measurement of Creep Stress Exponent of Ti6A14V Alloy at Room Temperature
Meng Longhui
Yang Yinfei
He Ning
RARE METAL MATERIALS AND ENGINEERING, 2016, 45 (03) : 617 - 622
[37] 铸造Ti6A14V合金的性能
材料工程, 1979, (03) : 1 - 5
[38] Effect of laser peening on friction and wear behavior of medical Ti6A14V alloy
Zhou, Jianzhong
Sun, Yunjie
Huang, Shu
Sheng, Jie
Li, Jing
Agyenim-Boateng, Emmanuel
OPTICS AND LASER TECHNOLOGY, 2019, 109 : 263 - 269
[39] Influence of thermal oxidation temperature on the microstructural and tribological behavior of Ti6A14V alloy
Wang, Song
Liao, Zhenhua
Liu, Yuhong
Liu, Weiqiang
SURFACE & COATINGS TECHNOLOGY, 2014, 240 : 470 - 477
[40] A constitutive relation and failure criterion for Ti6A14V alloy at impact rates of strain
Macdougall, DAS
Harding, J
JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1999, 47 (05) : 1157 - 1185

← 1 2 3 4 5 →