An experimental study on crack closure induced by laser peening in pre-cracked aluminum alloy 2024-T351 and fatigue life extension

被引：39
|
作者：
Hu, Yongxiang [1 ]
Cheng, Han [1 ]
Yu, Jianhua [1 ,2 ]
Yao, Zhenqiang [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mech Engn, State Key Lab Mech Syst & Vibrat, Shanghai 200240, Peoples R China
[2] AECC Commercial Aircraft Engine Co Ltd, Shanghai 200240, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2020年 / 130卷
关键词：
Laser peening; Damage; Fatigue crack propagation; Crack closure; Crack arrest; DIGITAL IMAGE CORRELATION; RESIDUAL-STRESS; GROWTH-PROPERTIES; MICROSTRUCTURE; DAMAGE; PROPAGATION; BEHAVIOR; MODEL; STEEL;
D O I：
10.1016/j.ijfatigue.2019.105232
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
This study investigates crack closure induced by laser peening (LP) and its effect on fatigue life extension of 2024-T351 aluminum alloy with initial fatigue crack. LP is applied directly in the initial fatigue crack region. This treatment leads to interesting observations of crack arrest that has not been reported before for LP, and significant fatigue life enhancement. The fatigue life of the LP-treated pre-cracked specimen is 412% and 44.7% higher than the untreated specimen and LP-treated specimen without pre-crack, respectively. The crack closure around the pre-crack resulting from the LP-induced plastic deformation is mainly responsible for fatigue life extension.
引用
收藏
页数：10
相关论文
共 50 条
  • [31] Effect of surface treatment on fatigue life of the aluminium alloy 2024-T351
    Moulinier, F
    Davenport, AJ
    Bowen, P
    Morgan, PC
    ADVANCES IN MECHANICAL BEHAVIOUR, PLASTICITY AND DAMAGE, VOLS 1 AND 2, PROCEEDINGS, 2000, : 1243 - 1249
  • [32] Experimental study on laser peen forming of aluminium alloy 2024-T351 plate
    Huang, X.
    Zeng, Y. S.
    Wang, M. T.
    Zou, S. K.
    19TH INTERNATIONAL CONFERENCE ON METAL FORMING, MF 2022, 2022, 1270
  • [33] Tensile Property and Fracture Analysis of 2024-T351 Aluminum Alloys by Cryogenic Laser Peening
    Sun Y.
    Zhou J.
    Sheng J.
    Huang S.
    Xu S.
    Li J.
    Xu G.
    Zhongguo Jiguang/Chinese Journal of Lasers, 2017, 44 (08):
  • [34] THE EFFECT OF ABSORBED HYDROGEN ON TORSIONAL FATIGUE OF 2024-T351 ALUMINUM-ALLOY
    MABIE, HH
    WILSON, JH
    LOUTHAN, MR
    KAUFFMAN, CJ
    SCRIPTA METALLURGICA, 1983, 17 (01): : 59 - 62
  • [35] In situ SEM measurements of crack closure for small fatigue cracks in aluminium 2024-T351
    Halliday, M.D.
    Poole, P.
    Bowen, P.
    Fatigue and Fracture of Engineering Materials and Structures, 1995, 18 (06): : 717 - 729
  • [36] ROLE OF HYDROGEN AND HUMIDITY IN THE TORSIONAL FATIGUE OF ALUMINUM-ALLOY 2024-T351
    SUDARSHAN, TS
    LOUTHAN, MR
    PLACE, TA
    MABIE, HH
    MATERIALS SCIENCE AND ENGINEERING, 1985, 73 (1-2): : 131 - 138
  • [37] Fatigue Assessment of 2024-T351 Aluminum Alloy Under Uniaxial Cyclic Loading
    Chabouk, Ehsan
    Shariati, Mahmoud
    Kadkhodayan, Mehran
    Nejad, Reza Masoudi
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (04) : 2864 - 2875
  • [38] The Effect of Surface Engineering Treatments on the Fatigue Behavior of 2024-T351 Aluminum Alloy
    C.A. Rodopoulos
    A.Th. Kermanidis
    E. Statnikov
    V. Vityazev
    O. Korolkov
    Journal of Materials Engineering and Performance, 2007, 16 : 30 - 34
  • [39] The effect of surface engineering treatments on the fatigue behavior of 2024-T351 aluminum alloy
    Rodopoulos, C. A.
    Kermanidis, A. Th.
    Statnikov, E.
    Vityazev, V.
    Korolkov, O.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2007, 16 (01) : 30 - 34
  • [40] Fatigue Assessment of 2024-T351 Aluminum Alloy Under Uniaxial Cyclic Loading
    Ehsan Chabouk
    Mahmoud Shariati
    Mehran Kadkhodayan
    Reza Masoudi Nejad
    Journal of Materials Engineering and Performance, 2021, 30 : 2864 - 2875
12345