Control of post-weld fracture toughness in friction stir processed X80 HSLA steel

被引：6
|
作者：
Crook, Nolan T. [1 ]
Nelson, Tracy W. [2 ]
机构：
[1] Brigham Young Univ, Dept Mech Engn, 350 EB, Provo, UT 84602 USA
[2] Brigham Young Univ, Dept Mfg Engn, 265 CTB, Provo, UT 84602 USA
来源：
ENGINEERING FRACTURE MECHANICS | 2022年 / 271卷
基金：
美国国家科学基金会;
关键词：
FSW; CTOD; X80; MICROSTRUCTURE; ZONE;
D O I：
10.1016/j.engfracmech.2022.108586
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
The present study investigates the fracture toughness of FSW X80 HSLA steel welds. Weld cooling rate and peak temperature were varied among welds; indirectly manipulated through FSW travel speed, rpm, and weld preheat. Fracture toughness was tested according to ASTM 1820 standard along the weld centerline using surface-notched SEB specimen cooled to -40 degrees C. Results demonstrate that CTOD of FSW X80 has a strong inverse linear correlation with post-weld cooling rate. Low cooling rate welds exhibited CTOD values consistently above those of base metal. Microstructure similar to the base metal can be recreated throughout the weld. Weld CTOD can be selected by controlling weld CR.
引用
收藏
页数：16
相关论文
共 50 条
  • [31] Simultaneously enhancing strength and fracture toughness via tailoring the microstructure in X80 girth weld metal
    Wang, Ce
    Li, Chengning
    Dai, Lianshuang
    Yang, Xiaocong
    Han, Jiawei
    Cui, Shaohua
    Yang, Zhenwen
    Di, Xinjie
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 29 : 3096 - 3107
  • [32] Effects of friction stir welding and post-weld annealing on nanostructured ferritic alloy
    Etienne, A.
    Cunningham, N.J.
    Wu, Y.
    Odette, G.R.
    Energy Materials: Materials Science and Engineering for Energy Systems, 2012, 6 (01): : 724 - 728
  • [33] Statistical Assessment of Fracture Toughness Results from the HAZ of X80 Pipeline FCAW Girth Weld
    Chen, Hongyuan
    Feng, Qingshan
    Bi, Ying
    Gao, Xiongxiong
    Dai, Lianshuang
    Chi, Qiang
    MATERIALS, 2022, 15 (17)
  • [34] Microstructural Evolution of HSLA ISO 3183 X80M (API 5L X80) Friction Stir Welded Joints
    Tahiana F. C. Hermenegildo
    Tiago F. A. Santos
    Edwar A. Torres
    Conrado R. M. Afonso
    Antonio J. Ramirez
    Metals and Materials International, 2018, 24 : 1120 - 1132
  • [35] Microstructure and fracture toughness of multipass friction stir welded joints of API-5L-X80 steel plates
    Avila, Julian A.
    Rodriguez, Johnnatan
    Mei, Paulo Roberto
    Ramirez, Antonio J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 673 : 257 - 265
  • [36] The influence of post-weld tempering temperatures on microstructure and strength in the stir zone of friction stir welded reduced activation ferritic/martensitic steel
    Li, Shengli
    Yang, Xinqi
    Vajragupta, Napat
    Tang, Wenshen
    Hartmaier, Alexander
    Li, Huijun
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2021, 814
  • [37] Influence of heat input on post weld microstructure and mechanical properties of friction stir welded HSLA-65 steel
    Wei, Lingyun
    Nelson, Tracy W.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 556 : 51 - 59
  • [38] Effect of friction stir welding and post-weld heat treatment on a nanostructured ferritic alloy
    Mazumder, B.
    Yu, X.
    Edmondson, P. D.
    Parish, C. M.
    Miller, M. K.
    Meyer, H. M., III
    Feng, Z.
    JOURNAL OF NUCLEAR MATERIALS, 2016, 469 : 200 - 208
  • [39] Effects of weld strength undermatch on fracture toughness of HAZ notched weldments in a HSLA steel
    Shi, YW
    Han, ZX
    Fu, JQ
    INTERNATIONAL JOURNAL OF FRACTURE, 1998, 91 (04) : 349 - 358
  • [40] Effects of weld strength undermatch on fracture toughness of HAZ notched weldments in a HSLA steel
    Shi, Yaowu
    Han, Zhunxiang
    Fu, Jianqin
    International Journal of Fracture, 91 (04): : 349 - 358
12345