Localized corrosion of a 2219 aluminium alloy exposed to a 3.5% NaCl solution

被引：130

作者：

Grilli, Rossana ^{[1
]}

Baker, Mark A. ^{[1
]}

Castle, James E. ^{[1
]}

Dunn, Barrie ^{[2
]}

Watts, John F. ^{[1
]}

机构：

[1] Univ Surrey, Fac Engn & Phys Sci, Surface Anal Lab, Surrey GU2 7XH, England

[2] European Space Technol Ctr, NL-2200 AG Noordwijk, Netherlands

来源：

CORROSION SCIENCE | 2010年 / 52卷 / 09期

关键词：

Aluminium alloy; Intermetallics; AES; Corrosion; PITTING CORROSION; INITIATION; SPECTROSCOPY; 2024-T3;

D O I：

10.1016/j.corsci.2010.04.035

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

This work is focused on the role of intermetallics in pitting corrosion of Al2219 alloy. Second phase particles were characterized by AES, SAM and EDX. Their behaviour in a solution of NaCl was investigated as a function of exposure time. The results confirmed the cathodic nature of the intermetallics with respect to the aluminium matrix. Corrosion products rich in aluminium and oxygen were found to progressively accumulate around the particles and iron was dissolved from the intermetallic, followed by back-deposition. Copper and manganese did not show any major activity. After 32 h of exposure the larger intermetallics were completely covered. (C) 2010 Elsevier Ltd. All rights reserved.

引用

页码：2855 / 2866

页数：12

共 50 条

[31] Corrosion resistance and antibacterial activity of 2-mercaptobenzothiazole for 7B04 aluminium alloy in 3.5%NaCl solution
Zhao, Zifei
Han, Ruifang
Yan, Xiaohan
Zhao, Xiaodong
Fan, Weijie
Xiao, Rongfeng
Liu, Yanqian
Yang, Jie
JOURNAL OF MOLECULAR STRUCTURE, 2025, 1321
[32] Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution
A. Venugopal
K. Sreekumar
V.S. Raja
Metallurgical and Materials Transactions A, 2010, 41 : 3151 - 3160
[33] Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution
Venugopal, A.
Sreekumar, K.
Raja, V. S.
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2010, 41A (12): : 3151 - 3160
[34] Effect of micro arc oxidation treatment on localized corrosion behaviour of AA7075 aluminum alloy in 3.5% NaCl solution
Venugopal, A.
Panda, Rajiv
Manwatkar, Sushant
Sreekumar, K.
Krishna, L. Rama
Sundararajan, G.
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (03) : 700 - 710
[35] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
Xing Qi
Bin Sun
Xiaoming Chen
Renguo Song
Journal of Wuhan University of Technology-Mater. Sci. Ed., 2020, 35 : 986 - 995
[36] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
祁星
SUN Bin
CHEN Xiaoming
宋仁国
JournalofWuhanUniversityofTechnology(MaterialsScience), 2020, 35 (05) : 986 - 995
[37] Corrosion Behavior of A356/SiC Alloy Matrix Composites in 3.5% NaCl Solution
Rodriguez Perez, Ociel
Garcia-Hinojosa, J. A.
Rodriguez Gomez, F. J.
Mejia-Sintillo, S.
Salinas-Bravo, V. M.
Lopes-Sesenez, R.
Gonzalez-Rodriguez, J. G.
Garcia-Perez, Cesar A.
INTERNATIONAL JOURNAL OF ELECTROCHEMICAL SCIENCE, 2019, 14 (08): : 7423 - 7436
[38] In-situ localized corrosion behavior of SiCp/Al composites in 3.5% NaCl aqueous solution
Cui, Xia
Zhou, Xianliang
Ouyang, Delai
Ye, Zhiguo
Zhu, Min
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2018, 124 (01):
[39] Localized Corrosion and Stress Corrosion Cracking Behavior of AA7003 in a 3.5 wt% NaCl Aqueous Solution
Qi, Xing
Sun, Bin
Chen, Xiaoming
Song, Renguo
JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2020, 35 (05): : 986 - 995
[40] Study on dealloying corrosion of QAl-9-2 alloy in 3.5% NaCl solution
Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (05): : 521 - 524

← 1 2 3 4 5 →