Microstructure and creep of Mo-ZrC in-situ composite

被引:16
|
作者
Suzuki, T [1 ]
Nomura, N [1 ]
Yoshimi, K [1 ]
Hanada, S [1 ]
机构
[1] Tohoku Univ, Inst Mat Res, Aoba Ku, Sendai, Miyagi 9808577, Japan
来源
MATERIALS TRANSACTIONS JIM | 2000年 / 41卷 / 09期
关键词
molybdenum; zirconium carbide; in-situ composite; hyper-eutectic structure; creep;
D O I
10.2320/matertrans1989.41.1164
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
Microstructure and creep of are-melted and annealed Mo-40 mol%ZrC in-situ composite were investigated in this study. Microstructure after annealing is found to consist of primary ZrC particles and fine Mo/ZrC eutectic structure, i.e. hyper-eutectic structure. Compressive creep tests in the temperature range from 1673 to 1873 K indicate that the stress exponent, n: is approximately 5 in the stress range from 100 to 500 MPa, and the apparent activation energy for the creep deformation is estimated to be about 500 kJ/mol at 200 MPa and 300 MPa. TEM observation for crept specimens shows that the creep deformation is accompanied with sub-boundary formation in Mo solid solution phase. It is suggested that the creep deformation of the composite in the temperature range examined is interpreted in terms of the dislocation creep of Mo solid solution phase controlled by the lattice diffusion of either Mo or Zr.
引用
收藏
页码:1164 / 1167
页数:4
相关论文
共 50 条
  • [21] Microstructure and mechanical properties of in-situ TiCp/2024 composite
    Ma, MZ
    Cai, DY
    Jing, TF
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2001, 17 : S65 - S68
  • [22] Microstructure and mechanical properties of in-situ TiCp/2024 composite
    Ma, M. (mamingzhen@0335.com), 2001, Chinese Society of Metals (17):
  • [23] THE MICROSTRUCTURE OF COPPER-25 CHROMIUM IN-SITU COMPOSITE
    Cao, H.
    Xian, A. P.
    PROCESSING AND FABRICATION OF ADVANCED MATERIALS XV, 2006, : 425 - 436
  • [24] Microstructure and wear resistance of in-situ synthesis ZrC-TiB2/Fe metal matrix composite coating by argon arc cladding
    王振廷
    殷力佳
    梁刚
    黑龙江科技大学学报, 2011, (03) : 219 - 222
  • [25] Behavior Characteristics of In-situ Formed ZrC Particle Reinforcement Composite Coating by Laser Cladding
    Yong, Yaowei
    Zhang, Xiang
    Fu, Wei
    Deng, Qilin
    Yang, Jianguo
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2018, 47 (05): : 1625 - 1630
  • [26] Phase transitions and microstructure evolutions of in-situ YSZ-ZrC composite coating under long-time plasma torch ablation
    Shao, Yu-xuan
    Yang, Yong
    Zhao, Ce-ce
    Tian, Wei
    SURFACE & COATINGS TECHNOLOGY, 2023, 466
  • [27] Behavior Characteristics of In-situ Formed ZrC Particle Reinforcement Composite Coating by Laser Cladding
    Yong Yaowei
    Zhang Xiang
    Fu Wei
    Deng Qilin
    Yang Jianguo
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (05) : 1625 - 1630
  • [28] Microstructure and mechanical properties of in-situ formed ZrC nanoparticles dispersion-strengthened tungsten alloy
    Cheng, X.
    Jing, K.
    Xie, Z. M.
    Liu, R.
    Wu, X. B.
    Wang, X. P.
    Fang, Q. F.
    Liu, C. S.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2022, 107
  • [29] Creep behavior of in-situ TiB fiber reinforced Ti matrix composite
    Kawabata, K
    Sato, E
    Kuribayashi, K
    CREEP AND FRACTURE OF ENGINEERING MATERIALS AND STRUCTURES, 2001, : 331 - 339
  • [30] Damage and failure during creep of a copper-chromium in-situ composite
    Carroll, HE
    Whitehouse, AF
    SCRIPTA MATERIALIA, 2000, 42 (12) : 1133 - 1137