Wear mechanisms of carbon bricks for no 1 blast furnace at Baoshan Iron and Steel Corporation

被引：0

作者：

Xie, MQ ^{[1
]}

机构：

[1] Baoshan Iron & Steel Corp, Iron & Steel Res Inst, Shanghai 201900, Peoples R China

来源：

UNIFIED INTERNATIONAL TECHNICAL CONFERENCE ON REFRACTORIES (UNITECR 97), VOL 1 - 3: 5TH BIENNIAL WORLDWIDE CONGRESS - REFRACTORIES, A WORLDWIDE TECHNOLOGY | 1997年

关键词：

D O I：

暂无

中图分类号：

TQ [化学工业];

学科分类号：

0817 ;

摘要：

After ten and half years service, the No.1 Blast furnace with an inner volume of 4063 m(3) at Baoshan Iron and Steel Corporation was blown out on April 1, 1996. A study on the wear mechanisms of carbon bricks shows that the penetration of iron and the deposition of zinc were the main reasons of the failure of carbon bricks.

引用

页码：1415 / 1422

页数：8

共 50 条

[21] Comparative Analysis on the Corrosion Resistance to Molten Iron of Four Kinds of Carbon Bricks Used in Blast Furnace Hearth
Wang, Cui
Zhang, Jianliang
Chen, Wen
Li, Xiaolei
Jiao, Kexin
Pang, Zhenping
Wang, Zhongyi
Wang, Tongsheng
Liu, Zhengjian
METALS, 2022, 12 (05)
[22] Charging System Enhancements for a Blast Furnace at Azovstal Iron and Steel Works Private Joint-Stock Corporation
Sosin, S. V.
Karikov, S. A.
Semakova, V. B.
Russkikh, V. P.
Semakov, V. V.
METALLURGIST, 2019, 63 (3-4) : 327 - 334
[23] BLAST-FURNACE OPERATION WITH HIGH PRODUCTIVITY AT KIMITSU NO 2 BLAST-FURNACE OF NIPPON-STEEL-CORPORATION
YAMAGUCHI, K
ISHIOKA, N
NAKAYAMA, M
FURUKAWA, T
MORII, K
ENDO, H
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 25 (03) : B86 - B86
[24] Coke Passivator in the Handan Iron and Steel Blast Furnace
Li Li-gang
Zhao Gui-xi
JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2009, 16 : 415 - 417
[25] BLAST-FURNACE OPERATION WITH HIGH PRODUCTIVITY AT KIMITSU NO-2 BLAST-FURNACE OF NIPPON-STEEL-CORPORATION
MORII, K
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (12): : S796 - S796
[26] The blast furnace and steel works of Frodingham Iron and Steel Co.
不详
ZEITSCHRIFT DES VEREINES DEUTSCHER INGENIEURE, 1928, 72 : 988 - 988
[27] OPERATION FOR PRODUCING THE PIG IRON WITH OPTIMUM QUALITIES AT KIMITSU NO. 2 BLAST FURNACE OF NIPPON STEEL CORPORATION.
Yamaguchi, Kazushige
Yamaguchi, Kazuyoshi
Nakayama, Masayuki
Morii, Kazuyuki
Nagata, Shunsuke
Kutsuzawa, Shigeru
Transactions of the Iron and Steel Institute of Japan, 1986, 26 (11)
[28] CONSTRUCTION AND BLOW IN OF MURORAN NO 2 BLAST-FURNACE OF NIPPON-STEEL-CORPORATION .2. BLOW IN OPERATION AT MURORAN NO 2 BLAST-FURNACE OF NIPPON-STEEL-CORPORATION
NARITA, T
TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1986, 72 (04): : S7 - S7
[29] Nodal wear model:: corrosion in carbon blast furnace hearths
Verdeja, LE
González, R
Alfonso, A
Barbés, MF
REVISTA DE METALURGIA, 2003, 39 (03) : 183 - 192
[30] WEAR MECHANISM OF ALUMINA-CARBON BRICKS BY MOLTEN STEEL
OKAMOTO, T
HASEGAWA, S
KAWAKAMI, T
KADOTA, Y
TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1983, 23 (05) : B164 - B164

← 1 2 3 4 5 →