THE INFLUENCE OF CONSOLIDATION PROCEDURE PARAMETERS ON COMPACTION OF Al POWDER

被引：0

作者：

Lowe, Terry C. ^{[1
]}

Kuncicka, Lenka ^{[2
,3
]}

Kocich, Radim ^{[2
,3
]}

Davis, Casey F. ^{[1
]}

Hlavac, Libor ^{[3
]}

Dvorak, Jiri ^{[4
]}

机构：

[1] Colorado Sch Mines, George S Ansell Dept Met & Mat Engn, Golden, CO 80401 USA

[2] VSB Tech Univ Ostrava, Fac Met & Mat Engn, Dept Mat Forming, Ostrava, Czech Republic

[3] VSB Tech Univ Ostrava, Reg Mat Sci & Technol Ctr, Ostrava, Czech Republic

[4] AS CR, Vvi, Inst Phys Mat, Brno, Czech Republic

来源：

METAL 2015: 24TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS | 2015年

关键词：

Aluminum powder; cold isostatic pressing; sintering; oxygen content; X-ray; HIGH-PRESSURE TORSION; MECHANICAL-PROPERTIES; COMPOSITES;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The influence of different consolidation procedures on compaction of Al powders was evaluated. Powder preparation procedures consisted of selection of particle size distribution, cold isostatic pressing (CIP), and vacuum sintering. Processing parameters investigated included the number of compression steps, compression pressure, and sintering temperature and time. Densities of the samples after compression and also after sintering were measured and compared. The overall oxygen content was analysed using by Energy Dispersive Spectroscopy. Phase composition was determined using X-ray. Microhardness measurements were performed to evaluate the degree of compaction. Double-step CIP at 200+ 300 MPa and subsequent sintering at 500 degrees C for 60 min produced the best combination of properties from all the consolidation technologies of Al particles. Of the particle size ranges studies, those with diameters between 20 and 45 mu m produced the best results. Aluminum oxide was present in the structure after all the processing treatments.

引用

页码：1352 / 1357

页数：6

共 50 条

[41] Influence of Milling and Compaction Processes on Magnetic Properties of FeCo Powder
Szumiata, T.
Gzik-Szumiata, M.
Brzozka, K.
Gawronski, M.
Gorka, B.
Kollar, P.
Oleksakova, D.
Polanski, K.
Szmaja, W.
ACTA PHYSICA POLONICA A, 2009, 115 (01) : 403 - 405
[42] Influence of Mechanical Alloying Parameters on Phase Formation in Al-Cu-Fe Powder
Mitka, M.
Litynska-Dobrzynska, L.
Goral, A.
Maziarz, W.
ACTA PHYSICA POLONICA A, 2014, 126 (04) : 984 - 987
[43] THE INFLUENCE OF THE MORPHOLOGY OF IRON POWDER PARTICLES ON THEIR COMPACTION IN AN AUTOMATIC DIE
Sustarsic, Borivoj
Godec, Matjaz
Donik, Crtomir
Paulin, Irena
Glodez, Srecko
Sori, Marko
Ratej, Milan
Javornik, Nada
MATERIALI IN TEHNOLOGIJE, 2015, 49 (02): : 303 - 309
[44] The influence of production modes of the electrocontact compaction on the porosity of the powder steel
T. A. Litvinova
S. N. Egorov
Russian Journal of Non-Ferrous Metals, 2011, 52 : 101 - 102
[45] Application experiences in powder compaction of iron powder influence of tool material on tool life
Sandberg, Odd
Krona, Andreas
Berg, Sigurd
Kaad, Flemming
Nord, Goran
PROGRESS IN POWDER METALLURGY, PTS 1 AND 2, 2007, 534-536 : 649 - +
[46] Influence of temperature on the compaction of an organic powder and the mechanical strength of tablets
Rouèche, E
Serris, E
Thomas, G
Périer-Camby, L
POWDER TECHNOLOGY, 2006, 162 (02) : 138 - 144
[47] On the influence from punch geometry on the stress distribution at powder compaction
Andersson, Daniel C.
Larsson, Per-Lennart
Cadario, Alessandro
Lindskog, Per
POWDER TECHNOLOGY, 2010, 202 (1-3) : 78 - 88
[48] COMPACTION OF A CERAMIC POWDER (ALUMINUM NITRIDE) AND INFLUENCE OF AN ULTRASOUND PULSE
MEXMAIN, J
JARRIGE, J
RIGONDAUD, B
ANNALES DE CHIMIE-SCIENCE DES MATERIAUX, 1991, 16 (08): : 581 - 594
[49] Design of ceramics powder compaction process parameters (Part II : Optimization)
Kim, J. L.
Keum, Y. T.
JOURNAL OF THE KOREAN CRYSTAL GROWTH AND CRYSTAL TECHNOLOGY, 2005, 15 (01): : 27 - 33
[50] Calculation of force parameters during compaction of powder materials in screw extruders
S. V. Atoyan
M. B. Generalov
N. S. Trutnev
Chemical and Petroleum Engineering, 1998, 34 : 730 - 734

← 1 2 3 4 5 →