Corrosion damage of stainless steels under atmospheric exposure conditions

被引：0
|
作者：
Burkert, Andreas [1 ]
Lehmann, Jens [1 ]
Burkert, Annette [1 ]
Mietz, Juergen [1 ]
机构：
[1] Korros & Korrosionsschutz, Fachgrp 6 1, Bundesanstalt Mat Forsch & Prufung BAM, D-12205 Berlin, Germany
来源：
STAHLBAU | 2010年 / 79卷 / 05期
关键词：
D O I：
10.1002/stab.201001288
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
Corrosion damage of stainless steels under atmospheric exposure conditions. In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products.
引用
收藏
页码：389 / 395
页数：7
相关论文
共 50 条
  • [21] Marine atmospheric stress corrosion cracking of austenitic stainless steels
    Kain, Robert M.
    Materials Performance, 1990, 29 (12) : 60 - 62
  • [22] Damage of stainless steel bars due to atmospheric corrosion
    Burkert, A.
    Lehmann, J.
    Burkert, A.
    Mietz, J.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2012, 63 (03): : 264 - 270
  • [23] Corrosion resistance and mechanical properties of low-alloy steels under atmospheric conditions
    Chen, YY
    Tzeng, HJ
    Wei, LI
    Wang, LH
    Oung, JC
    Shih, HC
    CORROSION SCIENCE, 2005, 47 (04) : 1001 - 1021
  • [24] Twelve year atmospheric exposure study of stainless steels in China
    Liang, CF
    Hou, WT
    OUTDOOR ATMOSPHERIC CORROSION, 2002, 1421 : 358 - 367
  • [25] Prediction of the life-time of austenitic stainless steels under stress corrosion cracking conditions
    Tandler, M
    Vehovar, L
    Vehovar, A
    METALURGIJA, 2001, 40 (02): : 71 - 75
  • [26] PITTING CORROSION BEHAVIOR OF STAINLESS STEELS IN NaCl SOLUTIONS UNDER HEAT TRANSFER CONDITIONS.
    Yasuda, Masaki
    Taga, Takehumi
    Ogata, Yukio
    Iida, Takaya
    Hine, Fumio
    Zairyo/Journal of the Society of Materials Science, Japan, 1986, 35 (396) : 1049 - 1053
  • [27] CORROSION OF STAINLESS-STEELS UNDER HEAT-TRANSFER CONDITIONS IN NITRIC-ACID
    ANDON, RJL
    PEMBERTON, RC
    THOMAS, JGN
    HARRISON, JM
    WORTHINGTON, SE
    SHAW, RD
    BRITISH CORROSION JOURNAL, 1986, 21 (02): : 119 - 128
  • [28] Stainless Steels and Corrosion
    Jenkins, Scott
    Chemical Engineering (United States), 2023, 130 (02):
  • [29] Influence of atmospheric pressure plasma treatments on the corrosion resistance of stainless steels
    Brunelli, K.
    Pezzato, L.
    Napolitani, E.
    Gross, S.
    Magrini, M.
    Dabala, M.
    METALLURGIA ITALIANA, 2014, (7-8): : 35 - 40
  • [30] Atmospheric corrosion behavior and estimation method of ordinarily used stainless steels
    Nippon Steel Corp, Kitakyushu, Japan
    Zairyo Kankyo, 1 (34-40):
12345