Fracture toughness of borides formed on boronized ductile iron

被引：47
|
作者：
Sen, U
Sen, S
Koksal, S
Yilmaz, F
机构：
[1] Sakarya Univ, Dept Met Educ, Tech Educ Fac, TR-54187 Sakarya, Turkey
[2] Sakarya Univ, Dept Met & Mat Engn, Fac Engn, TR-54187 Sakarya, Turkey
来源：
MATERIALS & DESIGN | 2005年 / 26卷 / 02期
关键词：
boronizing; ductile irons; hardness; fracture toughness;
D O I：
10.1016/j.matdes.2004.05.015
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, fracture toughness properties of boronized ductile iron were investigated. Boronizing was realized in a salt bath consisting of borax, boric acid and ferro-silicon. Boronizing heat treatment was carried out between 850 and 950 degreesC under the atmospheric pressure for 2-8 h. Borides e.g. FeB, Fe,13 formed on ductile iron was verified by X-ray diffraction (XRD) analysis, SEM and optical microscope. Experimental results revealed that longer boronizing time resulted in thicker boride layers. Optical microscope cross-sectional observation of borided layers showed dentricular morphology. Both microhardness and fracture toughness of borided surfaces were measured via Vickers indenter. The harnesses of borides formed on the ductile iron were in the range of 1160-2140 HV0.1 and fracture toughness were in the range of 2.19-4.47 MPa m(1/2) depending on boronizing time and temperature. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：175 / 179
页数：5
相关论文
共 50 条
  • [11] Influence of microstructure on fracture toughness of austempered ductile iron
    Rao, PP
    Putatunda, SK
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (07): : 1457 - 1470
  • [12] The growth kinetics of borides formed on boronized AISI 4140 steel
    Sen, S
    Sen, U
    Bindal, C
    VACUUM, 2005, 77 (02) : 195 - 202
  • [13] Dependence of fracture toughness of austempered ductile iron on austempering temperature
    Prasad Rao, P.
    Putatunda, Susil K.
    Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 1998, 29 A (12): : 3005 - 3016
  • [14] Dependence of fracture toughness of austempered ductile iron on austempering temperature
    P. Prasad Rao
    Susil K. Putatunda
    Metallurgical and Materials Transactions A, 1998, 29 : 3005 - 3016
  • [15] Investigations on the fracture toughness of austempered ductile iron alloyed with chromium
    Rao, PP
    Putatunda, SK
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 346 (1-2): : 254 - 265
  • [16] Fracture toughness of unalloyed austempered ductile cast iron (ADI)
    Department of Materials Science and Engineering, Wayne State University, Detroit
    MI
    48202, United States
    J Test Eval, 5 (325-332):
  • [17] The effect of testing temperature on fracture toughness of austempered ductile iron
    Hsu, CH
    Lee, SC
    Feng, HP
    Shy, YH
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2001, 32 (02): : 295 - 303
  • [18] Dependence of fracture toughness of austempered ductile iron on austempering temperature
    Rao, PP
    Putatunda, SK
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (12): : 3005 - 3016
  • [19] The effect of testing temperature on fracture toughness of austempered ductile iron
    Cheng-Hsun Hsu
    Shen-Chih Lee
    Yih-Hsun Shy
    Hui-Ping Feng
    Metallurgical and Materials Transactions A, 2001, 32 : 295 - 303
  • [20] Fracture toughness of bainite ductile iron obtained by continuously quenching
    Wei, Bingqing
    Liang, Ji
    Wu, Dehai
    Fu, Chengsong
    Gu, Chen
    Dong, Manlin
    Qinghua Daxue Xuebao/Journal of Tsinghua University, 1999, 39 (02): : 46 - 48
12345