Fracture toughness of borides formed on boronized ductile iron

被引：47
|
作者：
Sen, U
Sen, S
Koksal, S
Yilmaz, F
机构：
[1] Sakarya Univ, Dept Met Educ, Tech Educ Fac, TR-54187 Sakarya, Turkey
[2] Sakarya Univ, Dept Met & Mat Engn, Fac Engn, TR-54187 Sakarya, Turkey
来源：
MATERIALS & DESIGN | 2005年 / 26卷 / 02期
关键词：
boronizing; ductile irons; hardness; fracture toughness;
D O I：
10.1016/j.matdes.2004.05.015
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this study, fracture toughness properties of boronized ductile iron were investigated. Boronizing was realized in a salt bath consisting of borax, boric acid and ferro-silicon. Boronizing heat treatment was carried out between 850 and 950 degreesC under the atmospheric pressure for 2-8 h. Borides e.g. FeB, Fe,13 formed on ductile iron was verified by X-ray diffraction (XRD) analysis, SEM and optical microscope. Experimental results revealed that longer boronizing time resulted in thicker boride layers. Optical microscope cross-sectional observation of borided layers showed dentricular morphology. Both microhardness and fracture toughness of borided surfaces were measured via Vickers indenter. The harnesses of borides formed on the ductile iron were in the range of 1160-2140 HV0.1 and fracture toughness were in the range of 2.19-4.47 MPa m(1/2) depending on boronizing time and temperature. (C) 2004 Elsevier Ltd. All rights reserved.
引用
收藏
页码：175 / 179
页数：5
相关论文
共 50 条
  • [1] The fracture toughness of borides formed on boronized cold work tool steels
    Sen, U
    Sen, S
    MATERIALS CHARACTERIZATION, 2003, 50 (4-5) : 261 - 267
  • [2] Indentation fracture toughness of boronized unalloyed and alloyed ductile iron
    Toktas, Guelcan
    Korkmaz, Selman
    MATERIALS CHEMISTRY AND PHYSICS, 2023, 296
  • [3] An evaluation of some properties of borides deposited on boronized ductile iron
    Sen, U
    Sen, S
    Yilmaz, F
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2004, 148 (01) : 1 - 7
  • [4] Impact toughness and fracture toughness of austempered ductile iron
    ~*Jincheng LIU~1
    2. Dept. of Materials Science and Engineering
    China Foundry, 2004, (02) : 79 - 88
  • [5] The Fracture Toughness of Fe2B Formed on Boronized AISI 304
    Topuz, Polat
    Gundogdu, Emine
    Yilmaz, Eren
    Gumus, Emre
    MATERIALS TESTING, 2014, 56 (09) : 690 - 693
  • [6] Fracture toughness of austempered chilled ductile iron
    Hemanth, Joel
    Materials and Design, 1998, 19 (5-6): : 269 - 277
  • [7] Fracture toughness of austempered chilled ductile iron
    Hemanth, J
    MATERIALS & DESIGN, 1998, 19 (5-6): : 269 - 277
  • [8] Fracture toughness of austempered chilled ductile iron
    Hemanth, J
    MATERIALS SCIENCE AND TECHNOLOGY, 1999, 15 (08) : 878 - 884
  • [9] Constraint effects on fracture toughness of ductile cast iron in the ductile regime
    Lindqvist, S.
    Kuutti, J.
    Sirkia, L.
    Forsstrom, A.
    ENGINEERING FRACTURE MECHANICS, 2024, 306
  • [10] Influence of microstructure on fracture toughness of austempered ductile iron
    P. Prasad Rao
    Susil K. Putatunda
    Metallurgical and Materials Transactions A, 1997, 28 : 1457 - 1470
12345