INFLUENCE OF STRUCTURAL STATE ON CAVITATIONAL EROSION OF AUSTENITIC STAINLESS STEEL SOLUTION TREATMENT AND NITRIDING

被引：0
|
作者：
Padurean, Ioan [1 ]
Ionel, Ioana [1 ]
机构：
[1] Politehn Univ Timisoara, Mecan Fac, Timisoara, Romania
来源：
METALURGIA INTERNATIONAL | 2010年 / 15卷 / 10期
关键词：
cavitation erosion; nitriding; structural analyses; thermal treatment; microstructure;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
Samples of the austenitic stainless steel GX5CrNi19-10 have been thermally treated by solution treatment followed by nitriding After that treatment the samples of that stainless steel was tested at cavitation erosion In the areas affected by cavitation appear structure changes, micro cracks in a structure, separation and expulsions in structure Were obtained cavitation erosion resistance increases due to structural changes There were hardness and microstructure analysis Showed how steel structure influence on mass loss by cavitation. In conclusion, the thermal treatment of solution treatment followed by nitriding give a high cavitational erosion resistance to austenitic stainless steel GX5CrNi19-10.
引用
收藏
页码：55 / 59
页数：5
相关论文
共 50 条
  • [41] Initial phase formation during nitriding of austenitic stainless steel
    Manova, Darina
    Maendl, Stephan
    SURFACE & COATINGS TECHNOLOGY, 2023, 456
  • [42] SOME OBSERVATIONS ON PLASMA NITRIDING AUSTENITIC STAINLESS-STEEL
    DEARNLEY, PA
    NAMVAR, A
    HIBBERD, GGA
    BELL, T
    PLASMA SURFACE ENGINEERING, VOLS 1 AND 2, 1989, : 219 - 226
  • [43] Low temperature fluidized bed nitriding of austenitic stainless steel
    Haruman, E.
    Sun, Y.
    Malik, H.
    Sutjipto, A. G. E.
    Mridha, S.
    Widi, K.
    HEAT TREATMENT OF MATERIALS, 2006, 118 : 125 - +
  • [44] Technologies for low temperature carburising and nitriding of austenitic stainless steel
    Hertz, Domonique
    Lebrun, J.P.
    Michel, H.
    International Heat Treatment and Surface Engineering, 2008, 2 (01) : 32 - 38
  • [45] Solution nitriding applied to stainless steel parts
    Berns, H.
    Zaugg, R.
    HTM - Haerterei-Technische Mitteilungen, 2002, 57 (06): : 377 - 382
  • [46] Influence of temperature on layer growth as measured by in situ XRD observation of nitriding of austenitic stainless steel
    Manova, D.
    Guenther, C.
    Bergmann, A.
    Maendl, S.
    Neumann, H.
    Rauschenbach, B.
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2013, 307 : 310 - 314
  • [47] INFLUENCE OF NITRIDING AND LASER REMELTING ON PROPERTIES OF AUSTENITIC STAINLESS STEEL TYPE X10CrNi18-8 AND CAVITATION EROSION RESISTANCE
    Sitko, A.
    Szkodo, M.
    Kucharski, S.
    ADVANCES IN MATERIALS SCIENCE, 2016, 16 (02): : 21 - 31
  • [48] Comparison of Nitriding Behavior for Austenitic Stainless Steel 316Ti and Super Austenitic Stainless Steel 904L
    Maendl, Stephan
    Manova, Darina
    METALS, 2024, 14 (06)
  • [49] Novel plasma nitriding-oxidizing duplex treatment of AISI 316 austenitic stainless steel
    Abedi, H. R.
    Salehi, M.
    Yazdkhasti, M.
    MATERIALS LETTERS, 2010, 64 (06) : 698 - 701
  • [50] A.New surface treatment by pulsed plasma nitriding for chromium plated austenitic stainless steel
    Kuppusami, P
    Dasgupta, A
    Raghunathan, VS
    ISIJ INTERNATIONAL, 2002, 42 (12) : 1457 - 1460
12345