An experimental study on the dynamic fracture of extruded AA6xxx and AA7xxx aluminium alloys

被引:48
|
作者
Chen, Y. [1 ]
Pedersen, K. O. [2 ,3 ]
Clausen, A. H. [1 ,3 ]
Hopperstad, O. S. [1 ,3 ]
机构
[1] Norwegian Univ Sci & Technol, Dept Struct Engn, N-7034 Trondheim, Norway
[2] SINTEF Mat & Chem, Trondheim, Norway
[3] Norwegian Univ Sci & Technol, Ctr Res Based Innovat, SIMLab, N-7034 Trondheim, Norway
关键词
Instrumented Charpy tests; Ductile fracture; Intergranular fracture; Transgranular fracture; Precipitate-free zones; DUCTILE FRACTURE; MG ALLOY; BEHAVIOR; TOUGHNESS; STRENGTH; MICROSTRUCTURE; DEFORMATION; FORMABILITY; TEXTURE;
D O I
10.1016/j.msea.2009.06.007
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The dynamic fracture behaviour of extruded AA6xxx and AA7xxx aluminium alloys is investigated using an instrumented Charpy test machine and V-notch specimens. The specimens are made from extruded flat profiles with a rectangular cross-section of 10 mm thickness and 83 mm width. The material is in T6 temper, i.e. the peak hardness condition. The alloys have either recrystallized or fibrous grain structure. For each alloy six different Charpy impact tests are carried out in two series. In Series 1, the notch is parallel to the thickness direction of the profile (i.e. through the thickness), while the notch is perpendicular to the thickness direction in Series 2 (i.e. lying in the plane of the flat profile). In each series, the longitudinal direction of the specimen is parallel, 45 degrees or 90 degrees to the extrusion direction. Comprehensive fractographic investigations are carried out for the different tests and alloys. It is found that the dissipated energy is practically invariant to specimen orientation and notch direction for the recrystallized alloy. For the fibrous alloys the dissipated energy is lower when the longitudinal direction of the specimen is 90, to the extrusion direction, i.e. when the notch is parallel with the fibrous grain structure. Further, the energy dissipation is higher for Series 2 than for Series 1 due to substantial delamination and secondary cracking in Series 2. The precipitate-free zones (PFZs) formed adjacent to the grain boundary are weak areas, preferable for crack initiation and growth. This is seen in the fracture surface as facets with high density of small dimples and is more pronounced for specimens with the notch parallel to the fibre direction. (C) 2009 Elsevier B.V. All rights reserved.
引用
收藏
页码:253 / 262
页数:10
相关论文
共 50 条
  • [41] Microstructure in A356/AA6xxx after bimetallic casting with flux coating
    Bakke, Aina Opsal
    Arnberg, Lars
    Li, Yanjun
    JOINT 5TH INTERNATIONAL CONFERENCE ON ADVANCES IN SOLIDIFICATION PROCESSES (ICASP-5) & 5TH INTERNATIONAL SYMPOSIUM ON CUTTING EDGE OF COMPUTER SIMULATION OF SOLIDIFICATION, CASTING AND REFINING (CSSCR-5), 2019, 529
  • [42] Modeling of recrystallization behaviour of AA6xxx aluminum alloy during extrusion process
    Negozio, Marco
    Segatori, Antonio
    Pelaccia, Riccardo
    Reggiani, Barbara
    Di Donato, Sara
    Donati, Lorenzo
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2024, 34 (10) : 3170 - 3184
  • [43] IN SITU AA7XXX/TiB2 COMPOSITES PRODUCED BY FLUX ASSISTED SYNTHESIS
    Marcu, Dragos
    Moldovan, Petru
    Butu, Mihai
    Berbecaru, Andrei
    Cosac, Aurel
    UNIVERSITY POLITEHNICA OF BUCHAREST SCIENTIFIC BULLETIN SERIES B-CHEMISTRY AND MATERIALS SCIENCE, 2014, 76 (04): : 183 - 192
  • [44] Failure analysis of fusion clad alloy system AA3003/AA6xxx sheet under bending
    Shi, Y.
    Jin, H.
    Wu, P. D.
    Lloyd, D. J.
    Embury, D.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 610 : 263 - 272
  • [45] Effect of Testing Conditions, Gauge, and Temper on Stress Corrosion Cracking of AA7xxx Aluminum Aerospace Plate Alloys
    Warner, Timothy
    Koschel, Diana
    Whelchel, Ricky
    Smith, K. Paul
    Scamans, Geoff
    Merrill, Randall
    CORROSION, 2023, 79 (01) : 35 - 47
  • [46] Mechanical properties and constitutive behavior of as-cast high strength AA7xxx alloys below solidus temperature
    Bai, Q. L.
    Li, H. X.
    Du, Q.
    Zhang, J. S.
    Zhuang, L. Z.
    ALUMINIUM ALLOYS 2014 - ICAA14, 2014, 794-796 : 467 - +
  • [47] Precipitation in an extruded AA7003 aluminium alloy: Observations of 6xxx-type hardening phases
    Lervik, A.
    Marioara, C. D.
    Kadanik, M.
    Walmsley, J. C.
    Milkereit, B.
    Holmestad, R.
    MATERIALS & DESIGN, 2020, 186
  • [48] Application of the Nes Model for Static Recovery of the Dislocation Density in Cold Rolled AA6XXX
    Penlington, Alex
    Diak, Bradley
    Jin, Haiou
    ALUMINIUM ALLOYS 2014 - ICAA14, 2014, 794-796 : 605 - +
  • [49] Process Optimization of Friction Stir Welded AA7XXX and Steel With Different Preheating Conditions
    Humnabad, Prashant S.
    Prasad, M. S. Ganesha
    MATERIALS TODAY-PROCEEDINGS, 2019, 18 : 3556 - 3565
  • [50] ON THE CORRELATION OF SURFACE TEXTURE AND STRAIN INDUCED SURFACE ROUGHNESS IN AA6XXX ALUMINUM SHEET
    Kusters, S.
    Seefeldt, M.
    Van Houtte, P.
    MATERIALS PROCESSING AND TEXTURE, 2009, 200 : 731 - 742