Effect of compositional variation and fineness on the densification of MgO-Al2O3 compacts

被引：32

作者：

Sarkar, R ^{[1
]}

Banerjee, G ^{[1
]}

机构：

[1] Cent Glass & Ceram Res Inst, Refractory Div, Calcutta 700032, W Bengal, India

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 1999年 / 19卷 / 16期

关键词：

spinels; milling; sintering; solid state reaction; microstructure-final;

D O I：

10.1016/S0955-2219(99)00078-3

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Single stage densification of magnesia-alumina compacts were studied with MgO to Al2O3 molar ratios 1:1 (stoichiometric spinel), 2:1 (magnesia rich spinel) and 1,2 (alumina rich spinel). Attritor milling has been adopted to produce variation in fineness. Milling greatly improved the densification. Densification was found to be easier for the magnesia rich composition and difficult for the alumina rich one. Xray diffraction patterns showed the expected phases in stoichiometric and magnesia rich spinel. Alumina rich composition showed no free corundum phase on sintering at 1650 degrees C and only spinel phase marks the complete solid solution of excess alumina in spinel at this composition. EDAX analysis also supports the event and also reflects that the impurities are mainly present at the grain boundaries. (C) 1999 Elsevier Science Ltd. All rights reserved.

引用

页码：2893 / 2899

页数：7

共 50 条

[31] The effect of MgO and preparation techniques of the FeMnOδ/MgO-Al2O3 catalyst used for the vapor phase oxidation of cyclohexane
Yadav, Vijendra Kumar
Das, Taraknath
REACTION CHEMISTRY & ENGINEERING, 2022, 7 (11): : 2298 - 2312
[32] Preparation of MgO-Al2O3 binary gel system with mesoporous structure
Kirszensztejn, P
Przekop, R
Szymkowiak, A
Mackowska, E
Gaca, J
MICROPOROUS AND MESOPOROUS MATERIALS, 2006, 89 (1-3) : 150 - 157
[33] Magnesium-silicate-hydrate bonded MgO-Al2O3 castables
Hundere, A
Myhre, B
Odegård, C
Sandberg, B
Zhou, NS
Zhang, SH
Bi, ZY
Chen, ZQ
ADVANCES IN REFRACTORIES FOR THE METALLURGICAL INDUSTRIES III, 1999, : 135 - 150
[34] Modification kinetics of MgO-Al2O3 inclusions by Ca-treatment
1600, Ukrmetallurginform Scientific and Technical Agency Ltd (06):
[35] Acid-base properties of γ-Al2O3 and MgO-Al2O3 supported gold nanoparticles
Al-Daous, Mohammed A.
Manda, Abdullah A.
Hattori, Hideshi
JOURNAL OF MOLECULAR CATALYSIS A-CHEMICAL, 2012, 363 : 512 - 520
[36] A re-evaluation of the liquid phases in the CaO-Al2O3 and MgO-Al2O3 systems
Mao, HH
Selleby, M
Sundman, B
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2004, 28 (03): : 307 - 312
[37] Observations on densification of Al-Al2O3 composite powder compacts by pressure cycling
Jiang, G
Daehn, GS
Wagoner, RH
POWDER METALLURGY, 2003, 46 (01) : 78 - 82
[38] Effect of Addition of Non-oxides on the Slag Corrosion Resistance of MgO-Al2O3 Refractories
Morita, Keisuke
Sakida, Shinichi
Benino, Yasuhiko
Nanba, Tokuro
3RD INTERNATIONAL CONGRESS ON CERAMICS (ICC3): INNOVATION IN REFRACTORIES AND TRADITIONAL CERAMICS, 2011, 18
[39] MgO-Al2O3系浇注料的设计
沈继耀
谈家琪
成国祥
硅酸盐通报, 1998, (05) : 21 - 26+32
[40] DISCUSSION OF ACIDIC AND BASIC PROPERTIES OF MGO-AL2O3, MGO-SIO2 AND AL2O3-SIO2 MIXED OXIDES
VINEK, H
ZEITSCHRIFT FUR PHYSIKALISCHE CHEMIE-WIESBADEN, 1980, 120 (01): : 119 - 127

← 1 2 3 4 5 →