Effect of Initial Microstructure on Impact Toughness of 1200 MPa-Class High Strength Steel with Ultrafine Elongated Grain Structure

A medium-carbon low-alloy steel was prepared with initial structures of either martensite or bainite. For both initial structures, warm caliber-rolling was conducted at 773 K (500 degrees C) to obtain ultrafine elongated grain (UFEG) structures with strong < 110 >//rolling direction (RD) fiber deformation textures. The UFEG structures consisted of spheroidal cementite particles distributed uniformly in a ferrite matrix of a transverse grain size of about 331 and 311 nm in samples with initial martensite and bainite structures, respectively. For both initial structures, the UFEG materials had similar tensile properties, upper shelf energy (145 J), and ductile-to-brittle transition temperatures 98 K (500 degrees C). Obtaining the martensitic structure requires more rapid cooling than is needed to obtain the bainitic structure and this more rapid cooling promote cracking. As the UFEG structures obtained from initial martensitic and bainitic structures have almost identical properties, but obtaining the bainitic structure does not require a rapid cooling which promotes cracking suggests the use of a bainitic structure in obtaining UFEG structures should be examined further. (C) The Minerals, Metals & Materials Society and ASM International 2013