Development of IBAD/PLD process for long length Y-123 conductors in Fujikura

被引：19

作者：

Iijima, Y. ^{[1
]}

Kaneko, N. ^{[1
]}

Hanyu, S. ^{[1
]}

Sutoh, Y. ^{[1
]}

Kakirnoto, K. ^{[1
]}

Ajimura, S. ^{[1
]}

Saitoh, T. ^{[1
]}

机构：

[1] Fujikura Ltd, Koto Ku, Tokyo 1358512, Japan

来源：

PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2006年 / 445卷

关键词：

Y-123 coated conductors; ion-beam-assisted deposition (IBAD); pulsed-laser-deposition (PLD);

D O I：

10.1016/j.physc.2006.04.045

中图分类号：

O59 [应用物理学];

学科分类号：

摘要：

Long length manufacturing approach of YBa2Cu3O7-x (Y-123) conductor was performed using ion-beam-assisted-deposition (IBAD) and pulsed-laser-deposition (PLD) process in Fujikura Ltd. A new set of reel-to-reel MAD system was designed using 110 cm x 15 cm assisting ion source. The planer distribution of in-plane texture (Delta phi) for Gd2Zr2O7 template films were studied in large deposition area of 100 cm x 25 cm. The throughput of 5.5 m/h with Delta phi of 15 degrees was obtained for Gd2Zr2O7 films grown on 10 mm wide tapes. Long Y-123/CeO2/Gd2Zr2O7/Hastelloy tapes were produced by using reel-to-reel vacuum apparatuses of IBAD and PLD. I-c of 153 A, and 88 A were obtained in end-to-end of a 104 m long tape, and a 217 m long one, respectively. I-c of 360 A was obtained in a short sample with Y-123 thickness of 2.0 mu pm. A cryo-cooled 5-turn x 4-layer small solenoid coil with inner diameter of 60 mm was demonstrated using a Y-123 conductor formed by IBAD/PLD method. No severe heat spot was generated even the transporting current exceeded the coil I-c value of 355 A at 20 K. (c) 2006 Elsevier B.V. All rights reserved.

引用

页码：509 / 514

页数：6

共 50 条

[31] Development of Long REBCO Coated Conductors by PLD-REBCO/Sputter-CeO2/IBAD-MgO at SJTU and SSTC
Liu, L.
Li, Y.
Wu, X.
Xiao, G.
Xu, D.
IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2015, 25 (03)
[32] Comparison between Bi-2223 and Y-123 conductors for moderate-field HTS devices
Oomen, MP
Leghissa, M
Utz, B
Neumüller, HW
FRONTIERS IN SUPERCONDUCTING MATERIALS-NEW MATERIALS AND APPLICATIONS, 2004, 3 : 137 - 139
[33] Fabrication of long REBCO coated conductors by PLD process in China
Li, Yijie
Liu, Linfei
Wu, Xiang
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2015, 518 : 51 - 53
[34] Development of ion-beam-assisted-deposition method using pyrochlore type oxide buffer layers for Y-123 coated conductors
Iijima, Y
Kakimoto, K
Saitoh, T
Katoh, T
Hirayama, T
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2002, 66 (05) : 528 - 536
[35] Study of the synthesis process and structural defects in Y-123 superconducting systems by positron experiment
Chen, Z.P.
Zhang, J.C.
Cheng, G.S.
Li, X.G.
Zhang, X.S.
Wuli Xuebao/Acta Physica Sinica, 2001, 50 (03):
[36] Development of coated conductors by PLD process for HTS power applications
Ohmatsu, Kazuya
Abiru, Kenji
Yamaguchi, Takashi
Shingai, Yuki
Konishi, Masaya
SEI Technical Review, 2011, (73): : 45 - 51
[37] Study of the synthesis process and structural defects in Y-123 superconducting systems by positron experiment
Chen, ZP
Zhang, JC
Cheng, GS
Li, XC
Zhang, XS
ACTA PHYSICA SINICA, 2001, 50 (03) : 550 - 555
[38] Development of long GdBCO coated conductor using the IBAD/MPMT-PLD method
Ibi, A.
Fukushima, H.
Yamada, Y.
Miyata, S.
Kuriki, R.
Takahashi, K.
Shiohara, Y.
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2006, 19 (12): : 1229 - 1232
[39] Long-length IBAD-MgO buffer layers for high performance RE-123 coated conductors by a large ion beam source
Hanyu, S.
Tashita, C.
Hayashida, T.
Hanada, Y.
Morita, K.
Sutoh, Y.
Nakamura, N.
Kutami, H.
Igarashi, M.
Kakimoto, K.
Iijima, Y.
Saitoh, T.
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2010, 470 (20): : 1227 - 1229
[40] Development of long YBCO coated conductor by IBAD-PLD method -: Self-epitaxial PLD-CeO2 cap layer on IBAD buffer substrate
Muroga, T
Miyata, S
Watanabe, T
Iwai, H
Ibi, A
Yamada, Y
Izumi, T
Shiohara, Y
Kato, T
Hirayama, T
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2004, 68 (09) : 712 - 717

← 1 2 3 4 5 →