Solidification cracking susceptibility of ferritic stainless steels using Modified Varestraint Transvarestraint (MVT) method

被引：2
|
作者：
Konadu, D. S. [1 ,2 ]
Pistorius, P. G. H. [1 ]
Du Toit, M. [3 ]
Griesche, Axel [4 ]
机构：
[1] Univ Pretoria, Dept Mat Sci & Met Engn, ZA-0002 Pretoria, South Africa
[2] Univ Ghana, Dept Mat Sci & Engn, POB LG 77, Accra, Ghana
[3] Univ Wollongong, Sch Mech Mat Mechatron & Biomed Engn, Wollongong, NSW, Australia
[4] Fed Inst Mat Res & Testing, Bundesanstalt Materialforsch & Prufung BAM, Berlin, Germany
来源：
SADHANA-ACADEMY PROCEEDINGS IN ENGINEERING SCIENCES | 2019年 / 44卷 / 09期
关键词：
Modified Varestraint Transvarestraint; solidification cracking; ferritic stainless steel; microstructure; welding; susceptibility;
D O I：
10.1007/s12046-019-1175-0
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The Modified Varestraint Transvarestraint (MVT) test was used to investigate the solidification cracking susceptibility of an unstabilised, a Nb-stabilised and two (Ti + Nb) dual-stabilised ferritic stainless steels. Two different welding speeds of 6 and 3 mm/s using autogenous gas tungsten arc welding were employed. At the welding speed of 6 mm/s, the high-content (Ti + Nb) steel was resistant and the Nb-stabilised steel was marginally susceptible to solidification cracking. At the welding speed of 3 mm/s, the Nb and the high (Ti + Nb) steels were found to be marginally susceptible to solidification cracking while the unstabilised and low-content (Ti + Nb) grades were resistant to solidification cracking. The weld metal microstructures transverse to the welding direction revealed columnar grains in all the samples for both welding speeds. The ferritic stainless steels were generally resistant to solidification cracking, except the Nb-stabilised steel, which was marginally susceptible to solidification cracking.
引用
收藏
页数：6
相关论文
共 50 条
  • [31] The effect of solidification behaviour of austenitic stainless steel on the solidification cracking susceptibility
    刘仁培
    董祖珏
    潘永明
    China Welding, 2005, (01) : 38 - 43
  • [32] Influence mechanism of solidification mode on solidification cracking susceptibility of stainless steel
    Yamashita, Shotaro
    Yamauchi, Ryohei
    Saida, Kazuyoshi
    WELDING INTERNATIONAL, 2022, 36 (11) : 693 - 704
  • [33] Assessment of the Solidification Cracking Susceptibility of Welding Consumables in the Varestraint Test by Means of an Extended Evaluation Methodology
    Kromm, Arne
    Thomas, Maximilian
    Kannengiesser, Thomas
    Gibmeier, Jens
    Vollert, Florian
    ADVANCED ENGINEERING MATERIALS, 2022, 24 (06)
  • [34] SOLIDIFICATION AND SOLIDIFICATION CRACKING IN NITROGEN-STRENGTHENED AUSTENITIC STAINLESS STEELS.
    Ritter, Ann M.
    Savage Warren F.
    Metallurgical transactions. A, Physical metallurgy and materials science, 1986, 17 A (04): : 727 - 737
  • [35] SOLIDIFICATION AND SOLIDIFICATION CRACKING IN NITROGEN-STRENGTHENED AUSTENITIC STAINLESS-STEELS
    RITTER, AM
    SAVAGE, WF
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (04): : 727 - 737
  • [36] Back diffusion resisting solidification cracking in austenitic stainless steels
    Liang, Song-Mao
    Yu, Ping
    Zhang, Fan
    Kou, Sindo
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2021, 26 (08) : 606 - 613
  • [37] Study of Hot Cracking Behaviour of Nitrogen-Enhanced Austenitic Stainless Steels using Varestraint and Hot Ductility Tests
    Ganesan Srinivasan
    Murthy Divya
    Shaju K. Albert
    Arun Kumar Bhaduri
    Andreas Klenk
    D. R. Gopalakrishna Achar
    Welding in the World, 2010, 54 : R322 - R332
  • [38] Performance assessment of the (Trans)Varestraint tests for determining solidification cracking susceptibility when using welding processes with filler metal
    da Silva, CLM
    Scotti, A
    MEASUREMENT SCIENCE AND TECHNOLOGY, 2004, 15 (11) : 2215 - 2223
  • [39] COMPARISON OF STRESS-CORROSION CRACKING SUSCEPTIBILITY OF AUSTENITIC AND FERRITIC STAINLESS-STEELS IN SMALL PUNCH TESTING
    MISAWA, T
    OHTSUKA, T
    SEO, M
    SAITO, M
    JOURNAL OF NUCLEAR MATERIALS, 1991, 179 : 611 - 614
  • [40] HOT CRACKING SUSCEPTIBILITY OF AUSTENITIC STAINLESS-STEELS
    OGAWA, T
    TSUNETOMI, E
    WELDING JOURNAL, 1982, 61 (03) : S82 - S93
12345