Dielectric properties of Ti4+ substituted BaFe12O19 nanoparticles

Series of nanocrystalline BaTixFe12-(4/3)xO19 hexagonal ferrites, 0 <= x <= 1, was prepared using the chemical co-precipitation method. As-prepared samples were heated at 1200 degrees C for 20 h and slowly cooled to room temperature (RT). XRD studies proved that the samples have single phase M-type hexagonal nanostructure, where their grain size lies in the range of 42.4 - 61.3 nm. Their dielectric properties were studied against temperature (T) and frequency (F). DC conductivity showed increase against T, whereas AC conductivity showed increase with increasing both T and F. This proved the semiconducting behavior of the samples. Activation energies were found to lie in the range of 0.054-0.169 eV for temperature range of RT similar to 373 K and of 0.114-0.274 eV for higher temperatures up to 473 K. Variation of the dielectric constant and AC conductivity against F revealed dispersion in all these hexagonal nanostructures, which was assigned to Maxwell-Wagner type of interfacial polarization. Variation of the dielectric loss tangent against F showed a relaxation spectrum for all samples, whereas the dielectric constant and loss tangent showed an increasing trend against T. The relative magnetic permeability ae r showed an increasing trend with temperature.