EFFECT OF IMPACT COMPRESSION ON THE AGE-HARDENING OF RAPIDLY SOLIDIFIED AL-ZN-MG BASE ALLOYS

Effect of impact compression on the age-hardening behavior and the mechanical properties of Mesoalite aluminum alloy was examined by means of the high-velocity plane collision between a projectile and Mesoalite by using a single powder gun. By imposing the impact compression to the Meso10 and Meso20 alloys in the state of quenching after the solution heat treatment, the following age-hardening at 110 degrees C was highly increased, comparing with the Mesoalite without the impact compression. XRD results revealed that high plastic strain was introduced on the specimen inside after the impact compression. Compression test results also clarified that both Meso10 and Meso20 alloy specimens imposed the impact compressive stresses more than 5 GPa after the peak-aging at 110 degrees C showed higher yield stresses, comparing with the alloys without the impact compression. It was also shown that the Meso10 and Meso20 specimens after the solution heat treatment, followed by the high-velocity impact compression (12 GPa) and the peak-aging treatment indicated the highest compressive yield stresses such as 994 GPa in Meso 10 and 1091 GPa in Meso20.