A hot tearing criterion based on solidification microstructure in cast alloys

被引:31
|
作者
Hu, Bo [1 ]
Li, Zixin [1 ]
Li, Dejiang [1 ]
Ying, Tao [1 ]
Zeng, Xiaoqin [2 ]
Ding, Wenjiang [1 ,2 ]
机构
[1] Shanghai Jiao Tong Univ, Natl Engn Res Ctr Light Alloy Net Forming, Sch Mat Sci & Engn, 800 Dongchuan Rd, Shanghai 200240, Peoples R China
[2] Shanghai Jiao Tong Univ, State Key Lab Met Matrix Composites, 800 Dongchuan Rd, Shanghai 200240, Peoples R China
基金
中国国家自然科学基金;
关键词
Hot tearing; Microstructure; Magnesium alloys; Casting; Criterion; ALUMINUM-ALLOYS; SUSCEPTIBILITY; CRACKING;
D O I
10.1016/j.jmst.2021.06.071
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
A criterion based on solidification microstructure was proposed to precisely predict the hot tearing behavior of cast alloys, which takes into account the effects of both mechanical and nonmechanical factors. This criterion focuses on the events occurring at the grain boundary, which are determined by the thermal contraction, solidification shrinkage, grain growing and liquid feeding. This criterion responds to a series of factors that affect hot tearing, such as alloy composition, mold design, casting process and microstructure. Its credibility has been validated by studying the hot tearing behavior of Mg-Ce alloys. In conformity with the experimental results, this criterion predicted decrease in the number of rods occurring hot tearing with increasing cerium content. A simplified criterion was derived and validated by Mg-Ce (equiaxed grain) and Mg-Al (columnar grain) alloy systems, which is suitable for the case where the eutectic liquid fraction is low and the liquid feeding can be ignored. In addition, a hot tearing index for equiaxed grains was proposed, that is, vertical bar dT/d(f(s)(1/3))vertical bar near (fs)(1/3) = 1, and its prediction results were consistent with the hot tearing susceptibility calculated from the experimental results. (C) 2022 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
引用
收藏
页码:68 / 80
页数:13
相关论文
共 50 条
  • [21] Solidification process and hot tearing behaviors of AZ series magnesium alloys
    Zhou, Ye
    Mao, Pingli
    Wang, Zhi
    Zhou, Le
    Liu, Zheng
    Wang, Feng
    MATERIALS RESEARCH EXPRESS, 2019, 6 (11)
  • [22] Effect of adding Pr on the microstructure and hot tearing sensitivity of as-cast Al-Cu-Mg alloys
    Yue, Chunyu
    Yuan, Xiaoguang
    Wang, Yuxiang
    Su, Ming
    MATERIALS CHARACTERIZATION, 2022, 191
  • [23] A modified hot tearing criterion for direct chill casting of aluminium alloys
    Bai, Q. L.
    Liu, J. C.
    Li, H. X.
    Du, Q.
    Katgerman, L.
    Zhang, J. S.
    Zhuang, L. Z.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (08) : 846 - 854
  • [24] A study on the hot tearing in AL-1% Sn cast alloys
    Datta, G. L.
    Karunakar, D. B.
    PROCEEDINGS OF THE INSTITUTION OF MECHANICAL ENGINEERS PART B-JOURNAL OF ENGINEERING MANUFACTURE, 2006, 220 (07) : 1131 - 1139
  • [25] Reduction of Hot Tearing of Cast Semi-Solid 206 Alloys
    Lemieux, Alain
    Langlais, Joseph
    Chen, X-Grant
    SEMI-SOLID PROCESSING OF ALLOYS AND COMPOSITES XII, 2013, 192-193 : 101 - +
  • [26] Hot tearing evaluation of al - based alloys
    Bruna, Marek
    Sládek, Augustín
    Manufacturing Technology, 2016, 16 (02): : 323 - 327
  • [27] Solidification and microstructure of sand cast Mg-Al alloys
    Carlson, BE
    ADVANCED ENGINEERING MATERIALS, 2001, 3 (04) : 245 - 247
  • [28] Metallurgical Characterization of Hot Tearing Curves Recorded during Solidification of Magnesium Alloys
    Huang, Y. D.
    Wang, Z.
    Srinivasan, A.
    Kainer, K. U.
    Hort, N.
    ACTA PHYSICA POLONICA A, 2012, 122 (03) : 497 - 500
  • [29] Thermomechanical simulation and experimental characterisation of hot tearing during solidification of aluminium alloys
    He, Y.
    Li, S.
    Sadayappan, K.
    Apelian, D.
    INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2013, 26 (02) : 72 - 81
  • [30] Formation of hot tearing in directional solidification
    Ding, H
    Fu, HZ
    Liu, ZY
    Dong, XB
    RARE METAL MATERIALS AND ENGINEERING, 1997, 26 (01) : 19 - 21