The effect of ZnO addition on the electrochemical properties of the LaNi3.55Mn0.4Al0.3Co0.2Fe0.55 electrode used in nickel-metal hydride batteries
被引:16
|作者:
Dabaki, Y.
[1
]
Boussami, S.
[1
]
Khaldi, C.
[1
]
Takenouti, H.
[2
,3
]
ElKedim, O.
[4
]
Fenineche, N.
[5
]
Lamloumi, J.
[1
]
机构:
[1] Univ Tunis, Equipe Hydrures Metall, Lab Mecan Mat & Proc, ENSIT, 5 Ave Taha Hussein, Tunis 1008, Tunisia
[2] UPMC Univ Paris 06, Sorbonne Univ, LISE, UMR 8235, Case 133,4 Pl Jussieu, F-75252 Paris 05, France
[3] CNRS, UMR 8235, LISE, 4 Pl Jussieu, F-75252 Paris 05, France
[4] UTBM, FEMTO ST, MN2S, Site Sevenans, F-90010 Belfort, France
[5] UTBM, IRTES LERMPS, FR FCLAB, Site Sevenans, F-90010 Belfort, France
关键词:
Ni-MH batteries;
Catalyst;
Electrochemical techniques;
Redox kinetics;
Intermetallic alloy;
HYDROGEN STORAGE ALLOY;
NEGATIVE ELECTRODE;
SURFACE MODIFICATIONS;
DEHYDRIDING KINETICS;
OXIDES;
PERFORMANCE;
SUBSTITUTION;
MAGNESIUM;
CO3O4;
CO;
D O I:
10.1007/s10008-016-3458-2
中图分类号:
O646 [电化学、电解、磁化学];
学科分类号:
081704 ;
摘要:
The studied electrochemical properties of the LaNi3.55Mn0.4Al0.3Co0.2Fe0.55 alloy showed a rather poor performance. To improve them, ZnO, a doping agent at different small amounts (0, 1, or 2.5 wt%), was added to this base alloy. Then, the prepared electrodes were investigated by various electrochemical techniques. The maximum discharge capacity, obtained after the activation procedure, increased with the rise in ZnO content. The activation, as well as the reversibility of the hydrogen absorption/desorption process, were significantly improved with the addition of ZnO. It was observed that the latter did not affect considerably the stability and the cycling lifetime if added to the electrodes. After 30 charge/discharge cycles, the diffusion coefficients were estimated to be 1.55 x 10(-11), 1.30 x 10(-11), and 6.05 x 10(-11) cm(2) s(-1), respectively, for ZnO containing 0, 1, and 2.5 wt%. The ZnO catalyzed the kinetics of hydrogen absorption and desorption process thanks to capacity change before and after activation.