Fatigue characteristics of bearing steel in very high cycle fatigue

被引：10

作者：

Chana-Min, Suh ^{[2
]}

Jong-Hyoung, Kim ^{[1
]}

机构：

[1] Nagoya Univ, Grad Sch Engn, Dept Engn Sci & Mech, Chikusa Ku, Aichi 4648603, Japan

[2] Kyungpook Natl Univ, Sch Mech Engn, Taegu 702701, South Korea

来源：

JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY | 2009年 / 23卷 / 02期

关键词：

Very high cycle fatigue (VHCF); Rotational bending fatigue test; Shot peening; Fatigue characteristic; Fish-eye crack; Giga cycle fatigue; SUBSURFACE CRACK INITIATION; GIGACYCLE FATIGUE; MECHANISM; FAILURE;

D O I：

10.1007/s12206-008-1104-3

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Very high cycle fatigue (VHCF) tests were carried Out to find the fatigue characteristics of a super-long life range by using a cantilever type rotational bending fatigue test machine on three kinds of specimens in bearing steel which were quenched and tempered in air (A: non-shot peened and B: shot peened after heat treatment) and under vacuum environment(C: non-shot peened) in this Study. S-N curves obtained from the VHCF tests of the B and C specimens tend to come down again in the super-long life (10(9) cycles) range due to fish-eye type cracking, while most of the A and B specimens were fractured by surface detects Such Lis scratches and slip lines. This duplex S-N behavior of bearing steel has to be reviewed by the change of the fracture modes.

引用

页码：420 / 425

页数：6

共 50 条

[41] The behavior of short fatigue cracks during Very High Cycle (VHCF) Fatigue of duplex stainless steel
Krupp, U.
Giertler, A.
Soeker, M.
Fu, H.
Doenges, B.
Christ, H. -J.
Huesecken, A.
Pietsch, U.
Fritzen, C. -P.
Ludwig, W.
ENGINEERING FRACTURE MECHANICS, 2015, 145 : 197 - 209
[42] Very High Cycle Fatigue Behavior of SAE52100 Bearing Steel by Ultrasonic Nanocrystalline Surface Modification
Cho, In Shik
He, Yinsheng
Li, Kejian
Oh, Joo Yeon
Shin, Keesam
Lee, Chang Soon
Park, In Gyu
JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, 2014, 14 (11) : 8264 - 8269
[43] Influence of trace rare earth elements on very high cycle fatigue behavior of hot rolled bearing steel
Yang, Chaoyun
Li, Zan
Liu, Peng
Luan, Yikun
Li, Dianzhong
Li, Yiyi
Tariq, Naeem ul Haq
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
[44] A study on fatigue damage and crack initiation in austenitic steel matrix during very high cycle fatigue
Chai, Guocai
INTERNATIONAL JOURNAL OF FATIGUE, 2024, 179
[45] Influence of elevated temperature on the very high cycle fatigue properties of bearing steels
Schoenbauer, Bernd M.
More, Suraj S.
Morales-Espejel, Guillermo E.
Mayer, Herwig
INTERNATIONAL JOURNAL OF FATIGUE, 2023, 176
[46] The fatigue limit of bearing steels - Part I: A pragmatic approach to predict very high cycle fatigue strength
Lai, Junbiao
Lund, Thore
Ryden, Karin
Gabelli, Antonio
Strandell, Ingemar
INTERNATIONAL JOURNAL OF FATIGUE, 2012, 38 : 155 - 168
[47] Fatigue crack initiation site transition of high-strength steel under very high-cycle fatigue
Teng, Xiaoyuan
Pang, Jianchao
Gao, Chong
Li, Shouxin
Zhang, Zhefeng
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (12) : 4450 - 4464
[48] Short fatigue crack propagation during low-cycle, high cycle and very-high-cycle fatigue of duplex steel - An unified approach
Krupp, Ulrich
Alvarez-Armas, Iris
INTERNATIONAL JOURNAL OF FATIGUE, 2014, 65 : 78 - 85
[49] Thermal response of C45 steel in high and very high cycle fatigue
Ranc, Nicolas
Favier, Veronique
Munier, Bertrand
Vales, Frederic
Thoquenne, Guillaume
Lefebvre, Fabien
FATIGUE DESIGN 2015, INTERNATIONAL CONFERENCE PROCEEDINGS, 6TH EDITION, 2015, 133 : 265 - 271
[50] Very high cycle fatigue properties of bainitic high carbon-chromium steel
Mayer, H.
Haydn, W.
Schuller, R.
Issler, S.
Furtner, B.
Bacher-Hoechst, M.
INTERNATIONAL JOURNAL OF FATIGUE, 2009, 31 (02) : 242 - 249

← 1 2 3 4 5 →