EFFECT OF INITIAL TEMPERATURE ON THE MICROSTRUCTURE AND PROPERTIES OF CRYOGENIC ROLLED AZ31 MAGNESIUM ALLOY

被引：2

作者：

Wu, Zhenyu ^{[1
]}

Zhi, Chenchen ^{[1
,2
]}

Ma, Lifeng ^{[1
,2
]}

Zheng, Zebang ^{[3
]}

Zhu, Yanchun ^{[1
,2
]}

Jia, Weitao ^{[1
,2
]}

机构：

[1] Taiyuan Univ Sci & Technol, Coll Mech Engn, Taiyuan, Peoples R China

[2] Taiyuan Univ Sci & Technol, Minist Educ, Heavy Machinery Engn Res Ctr, Taiyuan, Peoples R China

[3] Northwestern Polytech Univ, Sch Mat Sci & Engn, State Key Lab Solidificat Proc, Shaanxi Key Lab High Performance Precis Forming T, Xian, Peoples R China

来源：

MATERIALI IN TEHNOLOGIJE | 2022年 / 56卷 / 05期

基金：

中国国家自然科学基金;

关键词：

cast-rolled AZ31 sheet; cryogenic rolling; microstructure; EBSD; STACKING-FAULT ENERGY; MECHANICAL-PROPERTIES; STRENGTH; DUCTILITY; EVOLUTION; TEXTURE; CU; BEHAVIOR;

D O I：

10.17222/mit.2022.443

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

By characterizing the properties of a twin cast-rolled AZ31 sheet after cryogenic rolling, the effects of the initial temperature on the microstructure and mechanical properties of the sheet obtained by cryogenic rolling were studied. The results indicate that the hardness of the alloy was a maximum due to the high-density dislocations in the microstructure when the initial temperature was room temperature. The highest yield strength and elongation appeared at the initial temperature of 200 degrees C, and the microstructure was mainly fine equiaxed grains. It was observed that fine grains increased, and the yield strength and elongation gradually decreased with the increase of the initial temperature. The overall trend of yield strength and elongation increased first and then decreased. Based on the results of different initial temperature treatments, the optimal microstructure and properties of AZ31 magnesium alloy were acquired when the initial temperature was 200 degrees C.

引用

页码：571 / 577

页数：7

共 50 条

[21] Evolution of microstructure and mechanical properties of AZ31 magnesium alloy rolled sheets during annealing
School of Mechanical Engineering, South China University of Technology, Guangzhou 510640, China
Jinshu Rechuli, 2007, 7 (8-12):
[22] Microstructure, Texture, and Mechanical Properties of Continuously Extruded and Rolled AZ31 Magnesium Alloy Sheets
Lili Guo
Rong Fu
Jiuyang Pei
Jianqiang Wang
Hongyang Zhao
Baoyun Song
Zhongchun Chen
Journal of Materials Engineering and Performance, 2019, 28 : 6692 - 6703
[23] Microstructure, Texture, and Mechanical Properties of Continuously Extruded and Rolled AZ31 Magnesium Alloy Sheets
Guo, Lili
Fu, Rong
Pei, Jiuyang
Wang, Jianqiang
Zhao, Hongyang
Song, Baoyun
Chen, Zhongchun
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (11) : 6692 - 6703
[24] Microstructure and mechanical property of rolled-weld magnesium alloy AZ31
Chen, Jian
Liu, Tianmo
Lu, Liwei
Zhang, Yueyang
Zeng, Wen
MATERIALS & DESIGN, 2012, 36 : 577 - 583
[25] Effect of temperature on tensile properties of hot rolled AZ31 Mg alloy
Balik, J.
Lukac, P.
Bohlen, J.
Kainer, K. U.
KOVOVE MATERIALY-METALLIC MATERIALS, 2007, 45 (03): : 135 - 140
[26] Effect of Mn content on tensile properties of rolled AZ31 magnesium alloy sheet
Yoshida, Y
Cisar, L
Sekine, T
Kamado, S
Kojima, Y
JOURNAL OF THE JAPAN INSTITUTE OF METALS, 2004, 68 (06) : 412 - 417
[27] Microstructure and properties of AZ31 magnesium alloy with rapid solidification
赵红亮
关绍康
郑飞燕
李庆奎
王利国
Transactions of Nonferrous Metals Society of China, 2005, (01) : 144 - 148
[28] Mechanical properties and microstructure of AZ31 magnesium alloy tubes
Luo, AA
Sachdev, AK
MAGNESIUM TECHNOLOGY 2004, 2004, : 79 - 85
[29] Microstructure and properties of AZ31 magnesium alloy with rapid solidification
Zhao, HL
Guan, SK
Zheng, FY
Li, QK
Wang, LG
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2005, 15 (01) : 144 - 148
[30] Effect of heat treatment on microstructure and properties of AZ31 magnesium alloy sheet
Chen, Hui-Fen, 1600, Northeast University (35):

← 1 2 3 4 5 →