Irradiation-controlled giant magnetoresistance of PtMn-based spin valve

被引：3
|
作者：
Huang, Sheng-Huang [1 ]
Lai, Chih-Huang [1 ]
Chiang, C. C. [1 ]
Yang, Cheng-Han [1 ]
机构：
[1] Natl Tsing Huang Univ, Dept Mat Sci & Engn, Hsinchu 30013, Taiwan
来源：
JOURNAL OF APPLIED PHYSICS | 2006年 / 99卷 / 08期
关键词：
D O I：
10.1063/1.2173603
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
He+-ion irradiation resulted in the direct ordering of PtMn without postannealing. Samples were irradiated with 2 MeV He+ ions and a beam current of 1.08 mu A/cm(2) such that the corresponding surface temperature was 190 degrees C. The exchange bias direction was set in situ during irradiation in a field of 900 Oe. A high giant magnetoresistance (GMR) ratio of 11% was obtained in PtMn-based spin valves after He+ irradiation. The GMR is completely eliminated after it is irradiated with oxygen ions at 42 keV. Combining He+ with oxygen-ion irradiation can provide magnetic patterning for GMR sensors. (C) 2006 American Institute of Physics.
引用
收藏
页数：3
相关论文
共 50 条
  • [21] Reduction of AMR effect in giant magnetoresistance spin valve structures
    Li, M
    Liao, SH
    Horng, C
    Zheng, Y
    Tong, RY
    Ju, K
    Dieny, B
    IEEE TRANSACTIONS ON MAGNETICS, 2001, 37 (04) : 1733 - 1735
  • [22] Spin-valve giant magnetoresistance films with antiferromagnetic PtPdMn
    Anderson, GW
    Huai, YM
    Miloslavsky, L
    Qian, CX
    Feng, Y
    JOURNAL OF APPLIED PHYSICS, 1999, 85 (08) : 6109 - 6111
  • [23] Tunneling vs. giant magnetoresistance in organic spin valve
    Yoo, Jung-Woo
    Jang, H. W.
    Prigodin, V. N.
    Kao, C.
    Eom, C. B.
    Epstein, A. J.
    SYNTHETIC METALS, 2010, 160 (3-4) : 216 - 222
  • [24] Giant magnetoresistance effect of spin valve Co/Pd/Co/NiO
    Gouda, W
    Shiiki, K
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1999, 205 (2-3) : 136 - 142
  • [25] QUANTUM-THEORY OF GIANT MAGNETORESISTANCE OF SPIN-VALVE SANDWICHES
    VEDYAYEV, A
    DIENY, B
    RYZHANOVA, N
    EUROPHYSICS LETTERS, 1992, 19 (04): : 329 - 335
  • [26] Angular dependence of giant magnetoresistance in spin-valve sandwiched structures
    Xu, M
    Mai, ZH
    PHYSICAL REVIEW B, 1999, 60 (13): : 9224 - 9227
  • [27] QUANTITATIVE INTERPRETATION OF GIANT MAGNETORESISTANCE PROPERTIES OF PERMALLOY-BASED SPIN-VALVE STRUCTURES
    DIENY, B
    EUROPHYSICS LETTERS, 1992, 17 (03): : 261 - 267
  • [28] Multilayer spin-valve CoFeP/Cu nanowires with giant magnetoresistance
    Sharko, S. A.
    Serokurova, A. I.
    Zubar, T. I.
    Trukhanov, S. V.
    Tishkevich, D. I.
    Samokhvalov, A. A.
    Kozlovskiy, A. L.
    Zdorovets, M. V.
    Panina, L. V.
    Fedosyuk, V. M.
    Trukhanov, A. V.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2020, 846 (846)
  • [29] Which spin valve for next giant magnetoresistance head generation? (invited)
    Araki, S
    Sano, M
    Li, S
    Tsuchiya, Y
    Redon, O
    Sasaki, T
    Ito, N
    Terunuma, K
    Morita, H
    Matsuzaki, M
    JOURNAL OF APPLIED PHYSICS, 2000, 87 (09) : 5377 - 5382
  • [30] Spin diffusion length and giant magnetoresistance in spin-valve tri-layers
    Hashimoto, Y
    Katsumoto, S
    Murayama, C
    Iye, Y
    PHYSICA B, 2000, 284 : 1247 - 1248
12345