Dynamic behavior to fatigue crack initiation of a glass/epoxy laminate

被引：0

作者：

Lecheb, S. ^{[1
]}

Nour, A. ^{[1
]}

Chellil, A. ^{[1
]}

Lechani, R. ^{[1
]}

Kebir, H. ^{[2
]}

机构：

[1] Univ Boumerdes, Lab Engines Dynam & Vibroacoust, Bumardas, Algeria

[2] Univ Technol Compiegne, Lab Roberval, Compiegne, France

来源：

ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII | 2014年 / 577-578卷

关键词：

Glass fiber; Polyester resin; Natural Frequencies; Crack Initiation; fracture;

D O I：

10.4028/www.scientific.net/KEM.577-578.677

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This paper based to study of the dynamic and fatigue behaviors with numerical and experimental parts of a composite material manufactured by stacking two layers of E-glass fiber in different angle orientations (0 degrees/90 degrees) immersed in polyester resin with total thickness 1.39mm. In Finite Element Analysis (FEA) using ABAQUS was used to evaluate the maximal (displacement, strain and stress) and the natural frequencies (mode shapes) of composite behavior under crack initiation condition. In the experimental part the laminate plate specimen with two layers is tested under one types of cyclic load in fully reversible tensile at (R=0), the fast fracture occur phenomenon and the fatigue life are presented, the fatigue testing exerted in INSTRON 8801 machine.

引用

页码：677 / +

页数：2

共 50 条

[21] Interlaminar shear fatigue behavior of glass/epoxy and carbon/epoxy composites
Makeev, Andrew
COMPOSITES SCIENCE AND TECHNOLOGY, 2013, 80 : 93 - 100
[22] Torsion fatigue behavior of unidirectional carbon/epoxy and glass/epoxy composites
Ogasawara, Toshio
Onta, Keiji
Ogihara, Shinji
Yokozeki, Tomohiro
Hara, Eiichi
COMPOSITE STRUCTURES, 2009, 90 (04) : 482 - 489
[23] FATIGUE CRACK INITIATION
WAYMAN, ML
ENGINEERING FRACTURE MECHANICS, 1979, 11 (02) : 463 - 463
[24] Fracture and fatigue study of unidirectional glass/epoxy laminate under different mode of loading
Kenane, M.
Benmedakhene, S.
Azari, Z.
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2010, 33 (05) : 284 - 293
[25] An ultrasonic method for dynamic monitoring of fatigue crack initiation and growth
Mi, B
Michaels, JE
Michaels, TE
JOURNAL OF THE ACOUSTICAL SOCIETY OF AMERICA, 2006, 119 (01): : 74 - 85
[26] The effect of surface treatments on interfacial fatigue crack initiation in aluminum/epoxy bonds
Lefebvre, DR
Ahn, BK
Dillard, DA
Dillard, JG
INTERNATIONAL JOURNAL OF FRACTURE, 2002, 114 (02) : 191 - 202
[27] Fatigue crack propagation behavior of interpenetrating vinylester/epoxy resins
Szabó, JS
Gryshchuk, O
Karger-Kocsis, J
JOURNAL OF MATERIALS SCIENCE LETTERS, 2003, 22 (16) : 1141 - 1145
[28] The effect of surface treatments on interfacial fatigue crack initiation in aluminum/epoxy bonds
D.R. Lefebvre
B.K. Ahn
D.A. Dillard
J.G. Dillard
International Journal of Fracture, 2002, 114 : 191 - 202
[29] Fatigue crack propagation and delamination behavior of advanced fiber metal hybrid laminate
Huang, Xiao
Liu, Jian-Zhong
Hangkong Cailiao Xuebao/Journal of Aeronautical Materials, 2012, 32 (05): : 97 - 102
[30] Fatigue crack initiation and early growth in the multilayered fibre-metal laminate GLARE 2
Vasek, A
Polak, J
Vogelesang, LB
ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 1685 - 1690

← 1 2 3 4 5 →