Ion-isotopic exchange reaction kinetics using organic base anion exchange resins Indion-102 and Indion GS-400

The present study deals with the kinetic study of iodide and bromide ion-isotopic exchange reactions in organic based anion exchange resins Indion-102 (nuclear grade) and Indion GS-400 (non-nuclear grade) using radiotracer isotopes. The resins in iodide and bromide form were equilibrated respectively with iodide and bromide ion solutions which were previously spiked with I-131 and Br-82 radiotracer isotopes. For both bromide and iodide ion-isotopic exchange reactions, it was observed that the values of specific reaction rate increase with increase in ion concentration from 0.001 to 0.004 M at a constant temperature of 40.0A degrees C. However, at constant ion concentration of 0.003 M, the specific reaction rate was observed to decrease with rise in temperature from 30.0 to 45.0A degrees C. Also it was observed that for iodide ion-isotopic exchange reaction by using Indion-102 resin, the values of specific reaction rate, amount of iodide ion exchanged, initial rate of iodide ion exchange and logK (d) were 0.258 min(-1), 0.492 mmol, 0.127 mmol/min and 19.2, respectively, which were higher than 0.208 min(-1), 0.416 mmol, 0.087 mmol/min and 17.6, respectively, obtained by using Indion GS-400 resin under identical experimental conditions of 40.0A degrees C, 1.000 g of ion exchange resin and 0.003M labeled iodide ion solution. The same trend was observed for the two resins during bromide ion-isotopic exchange reaction. The overall results indicate that, under identical experimental conditions, Indion-102 resin shows higher performance than Indion GS-400 resin.