Nondestructive evaluation of creep damage and life prediction of Ni-base superalloy used in advanced gas turbine blades by electrochemical technique

被引：0
|
作者：
Komazaki, S [1 ]
Shoji, T [1 ]
Abe, I [1 ]
Okada, I [1 ]
机构：
[1] Tohoku Univ, Grad Sch Engn, Res Inst Fracture Technol, Sendai, Miyagi 9808579, Japan
来源：
NONDESTRUCTIVE CHARACTERIZATION OF MATERIALS IX | 1999年 / 497卷
关键词：
D O I：
暂无
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
In order to develop a creep life assessment technique for directionally solidified Ni-base superalloy CM247LC, changes in electrochemical properties due to creep have been investigated. Experimental results on electrochemical polarization measurements revealed that the peak current density "Ip" and "Ipr" which appeared at a specific potential during potentiodynamic polarization reactivation measurements in dilute glyceregia solution linearly increased with a life fraction in early stage of the creep life and were uniquely correlated with Arrhenius type parameter "(t/tr)exp(-Qc/RT)". As a consequence, the creep life fraction can be estimated with high accuracy by the electrochemical technique.
引用
收藏
页码：113 / 119
页数：7
相关论文
共 50 条
  • [31] EFFECT OF STRAIN RATE ON THE CREEP-FATIGUE DAMAGE OF POLYCRYSTALLINE NI-BASE SUPERALLOY AT ELEVATED TEMPERATURE
    Nakayama, Koki
    Miura, Hideo
    PROCEEDINGS OF ASME 2022 INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, IMECE2022, VOL 9, 2022,
  • [32] AN INVESTIGATION OF CREEP CRACK-GROWTH OF RENE N4 ADVANCED NI-BASE SUPERALLOY
    KHOBAIB, M
    VENKATARAMAN, S
    NICHOLAS, T
    JOURNAL OF METALS, 1985, 37 (08): : A17 - A17
  • [33] Microstructure and mechanical behavior of mechanically alloyed ODS Ni-base superalloy for aerospace gas turbine application
    Park, LJ
    Ryu, HJ
    Hong, SH
    Kim, YG
    ADVANCED PERFORMANCE MATERIALS, 1998, 5 (04): : 279 - 290
  • [34] Brittle fracture of gas turbine blade caused by the formation of primary β-NiAl phase in Ni-base superalloy
    Zheng, Liang
    Xiao, Chengbo
    Zhang, Guoqing
    ENGINEERING FAILURE ANALYSIS, 2012, 26 : 318 - 324
  • [35] CREEP DAMAGE ASSESSMENT OF NOTCHED MATERIAL MADE OF A SOLIDIFICATION CONTROL NI-BASE SUPERALLOY USING THE EBSD METHOD
    Kobayashi, Daisuke
    Takeuchi, Tsutomu
    Nakabeppu, Katsushi
    PROCEEDINGS OF THE ASME POWER CONFERENCE JOINT WITH ICOPE-17, 2017, VOL 2, 2017,
  • [36] DEVELOPMENT OF A NEW NI-BASE SUPERALLOY FOR INDUSTRIAL GAS-TURBINE COMBUSTOR BY STATISTICAL ALLOY DESIGN METHOD
    TSUJI, I
    OKADA, K
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1991, 77 (04): : 574 - 581
  • [37] Fatigue life evaluation of a single crystal Ni-base superalloy, accompanying with change of microstructural morphology
    Sakaguchi, Motoki
    Okazaki, Masakazu
    INTERNATIONAL JOURNAL OF FATIGUE, 2007, 29 (9-11) : 1959 - 1965
  • [38] EFFECT OF ALLOYING ELEMENTS ON CREEP AND FATIGUE DAMAGE OF NI-BASE SUPERALLOY CAUSED BY STRAIN-INDUCED ANISOTROPIC DIFFUSION
    Suzuki, Ken
    Sano, Tomohiro
    Miura, Hideo
    PROCEEDINGS OF THE ASME INTERNATIONAL MECHANICAL ENGINEERING CONGRESS AND EXPOSITION, 2013, VOL 9, 2014,
  • [39] Formation of the Al-rich phase on grain boundary and the creep damage mechanism in directionally solidified Ni-base superalloy
    Komazaki, S
    Shoji, T
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (09): : 1945 - 1949
  • [40] Formation of the Al-Rich phase on grain boundary and the creep damage mechanism in directionally solidified Ni-base superalloy
    S. Komazaki
    T. Shoji
    Metallurgical and Materials Transactions A, 1997, 28 : 1945 - 1949
12345