The Formation Mechanism of Porosity for Spray-deposited 7075 Alloy

被引：6
|
作者：
Cao, Fuyang [1 ]
Li, Haichao [1 ]
Ning, Zhiliang [1 ]
Jia, Yandong [1 ]
Gu, Xu [1 ]
Yu, Lei [1 ]
Liu, Zuyan [1 ]
Sun, Jianfei [1 ]
机构：
[1] Harbin Inst Technol, Sch Mat Sci & Engn, Harbin 150001, Peoples R China
来源：
MATERIALS RESEARCH-IBERO-AMERICAN JOURNAL OF MATERIALS | 2015年 / 18卷
基金：
中国国家自然科学基金;
关键词：
spray deposition; superheat; porosity distribution; formation mechanism; FORMING PROCESS; MODEL; SOLIDIFICATION; ATOMIZATION; DROPLET;
D O I：
10.1590/1516-1439.328414
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The distribution model of temperature for the billets was established based on the porosity formation mechanism. By calculating the numerical relationship between the temperature of the deposition layer and the formation ability of the porosity, the distribution of porosity for spray formed 7075 aluminum billets was predicted and the influence of superheat on the formation probability of porosity was analyzed. The results show that a denser billet can be obtained with the average temperature of 813 K of the droplets and a liquid fraction of 50%. The porosity would increase whether the temperature further increased or decreased. Finally, the 7075 aluminum alloy was prepared by spray deposition technique with the optimum process parameters. It can be found that the distribution and types of the porosity were different at different locations. These results are in good agreement with the porosity distribution law.
引用
收藏
页码：89 / 94
页数：6
相关论文
共 50 条
  • [31] Superplastic behavior of spray-deposited 5083 Al
    Univ of California, Irvine, United States
    Metall Mat Trans A Phys Metall Mat Sci, 4 (1059-1068):
  • [32] Superplastic behavior of spray-deposited 5083 Al
    Wu, Y
    DelCastillo, L
    Lavernia, EJ
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (04): : 1059 - 1068
  • [33] Characteristics of spray-deposited CdSe thin films
    Elango, T
    Subramanian, V
    Murali, KR
    SURFACE & COATINGS TECHNOLOGY, 2000, 123 (01): : 8 - 11
  • [34] Superplastic behavior of spray-deposited 5083 Al
    Yue Wu
    Linda Del Castillo
    Enrique J. Lavernia
    Metallurgical and Materials Transactions A, 1997, 28 : 1059 - 1068
  • [35] Microstructure and phase formation in spray-deposited Al-18%Si-5%Fe-1.5%Cu alloy
    Srivastava, VC
    Ghosal, P
    Ojha, SN
    MATERIALS LETTERS, 2002, 56 (05) : 797 - 801
  • [36] Characterization of microstructure evolution and mechanical properties of the spray-deposited AZ31 magnesium alloy
    Yongbing Li Jinfeng Huang Hua Cui kai Tao Kui Zhang and Jishan Zhang State Key Laboratory for Advanced Metals and Materials University of Science and Technology Beijing Beijing China School of Materials Science and Engineering University of Science and Technology Beijing Beijing China Beijing General Research Institute for Nonferrous Metals Beijing China
    Journal of University of Science and Technology Beijing, 2008, 15 (06) : 740 - 746
  • [37] Superplastic deformation behavior of a spray-deposited eutectic NiAl/Cr(Mo) alloy doped with Dy
    Du, Xinghao
    Wu, Baolin
    Huang, J. C.
    INTERNATIONAL JOURNAL OF MATERIALS RESEARCH, 2007, 98 (02) : 123 - 127
  • [38] Characterization of microstructure evolution and mechanical properties of the spray-deposited AZ31 magnesium alloy
    Li, Yongbing
    Huang, Jinfeng
    Cui, Hua
    Tao, Kai
    Zhang, Kui
    Zhang, Jishan
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2008, 15 (06): : 740 - 746
  • [39] Characterization of microstructure evolution and mechanical properties of the spray-deposited AZ31 magnesium alloy
    Yongbing Li1)
    International Journal of Minerals,Metallurgy and Materials, 2008, (06) : 740 - 746
  • [40] Second Phase and Texture of Spray-Deposited Magnesium Alloy Containing Nd with Different Rolling Directions
    Liu F.
    Li Z.
    Li X.
    Sun H.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2018, 42 (05): : 463 - 469
12345