A user-friendly heat-resistant modified polymer-based adhesive for joining and repair of carbon/carbon composites

被引：15
|
作者：
Wang, Mingchao [1 ]
Hu, Xiaoxia [1 ]
Xu, Xiqing [1 ]
Yun, Ziqi [1 ]
Liu, Jiachen [1 ]
Du, Haiyan [1 ]
Guo, Anran [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Minist Educ, Key Lab Adv Ceram & Machining Technol, Tianjin 300072, Peoples R China
来源：
MATERIALS & DESIGN | 2015年 / 86卷
基金：
中国国家自然科学基金;
关键词：
Carbon-carbon composites; Polymers; Joining; High-temperature; Bonding strength; CARBON COMPOSITES; C/C COMPOSITES; TEMPERATURE;
D O I：
10.1016/j.matdes.2015.07.178
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A user-friendly heat-resistant modified polymer-based adhesive was developed to join C/C composites. After calcination at 1300 degrees C, the bonding effect of the adhesive reached the highest as more heat-resistant ceramics and high-temperature melting glass were generated in the adhesive. Its bonding strength was kept above 15 MPa during test from RT to 500 degrees C and the corresponding joints ruptured at C/C substrates. Besides, after repeated thermal-cycling at 1300 degrees C, the bonding strength at this temperature was maintained at about 12 MPa. For cured adhesive without calcination, its bonding strength could be maintained above 5 MPa during the whole heating process, which made it to have direct application in practice after curing. (C) 2015 Elsevier Ltd. All rights reserved.
引用
收藏
页码：709 / 713
页数：5
相关论文
共 50 条
  • [41] Polyvinyl acetate-glycidyl methacrylate co-polymer emulsion-based heat-resistant wood adhesive
    Gadhave, Ravindra V.
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2024,
  • [42] Low-speed impact behavior of fiber-reinforced polymer-based glass, carbon, and glass/carbon hybrid composites
    Saylik, Ahmet
    Temiz, Semsettin
    MATERIALS TESTING, 2022, 64 (06) : 820 - 831
  • [43] Elastomeric conductive composites based on conducting polymer-modified carbon black
    Zucolotto, V
    Avlyanov, J
    Mattoso, LHC
    POLYMER COMPOSITES, 2004, 25 (06) : 617 - 621
  • [44] Fabrication of organo-modified carbon nanotube with excellent heat resistance and preparation of its polymer-based nanocomposite by simple melt compounding
    Abiko, Yoshinori
    Hayasaki, Takuto
    Hirayama, Shuhei
    Almarasy, Ahmed A.
    Fujimori, Atsuhiro
    POLYMER BULLETIN, 2021, 78 (03) : 1585 - 1607
  • [45] Manufacture and Characterization of Heat-Resistant and Heat-Insulating New Composites Based on Resol Resin-Carbon Fibers-Perlite for the Built Heritage Protection
    Soupionis, George
    Zoumpoulakis, Loukas
    SCANNING, 2019, 2019
  • [46] Improvements in interfacial and heat-resistant properties of carbon fiber/methylphenylsilicone resins composites by incorporating silica-coated multi-walled carbon nanotubes
    Wu, Guangshun
    Ma, Lichun
    Wang, Yuwei
    Liu, Li
    Huang, Yudong
    JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2016, 30 (02) : 117 - 130
  • [47] Fabrication of organo-modified carbon nanotube with excellent heat resistance and preparation of its polymer-based nanocomposite by simple melt compounding
    Yoshinori Abiko
    Takuto Hayasaki
    Shuhei Hirayama
    Ahmed A. Almarasy
    Atsuhiro Fujimori
    Polymer Bulletin, 2021, 78 : 1585 - 1607
  • [48] MOFs meets wood: Renewable, self-supporting carbon-based composites for electromagnetic interference shielding with heat-resistant and electrothermal management
    Rong, Yujun
    Zhou, Xin
    Jiang, Shaohua
    Zhu, Wenkai
    Wang, Hanwei
    Dang, Baokang
    Sun, Qingfeng
    Ma, Xiaofan
    CHEMICAL ENGINEERING JOURNAL, 2025, 503
  • [49] Typical synergistic effect of graphite nanoplatelets and carbon nanotubes and its influence on polymer-based dielectric composites
    Zhao, Hang
    Yang, Minhao
    He, Delong
    Liu, Yu
    Bai, Jintao
    Wang, Hui
    Chen, Haowei
    Bai, Jinbo
    HIGH VOLTAGE, 2016, 1 (04): : 140 - 145
  • [50] Tunable and efficient electromagnetic wave absorption of carbon material modulating magnetic ionic polymer-based composites
    Ding, Changwei
    Xia, Wenlai
    Zhang, Shixian
    Li, Chenjian
    Liao, Xinyu
    Liu, Man
    Chen, Junyu
    Yu, Yueliang
    Qin, Shiyu
    Xiong, Chuanxi
    COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, 2023, 676
12345