Fracture and fatigue behavior of sintered steel at elevated temperatures: Part II. Fatigue crack propagation

被引：8
|
作者：
Shan, ZH [1 ]
Leng, Y
机构：
[1] Georgia Inst Technol, Sch Mat Sci & Engn, Atlanta, GA 30332 USA
[2] Hong Kong Univ Sci & Technol, Dept Engn Mech, Kowloon, Peoples R China
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 1999年 / 30卷 / 11期
关键词：
D O I：
10.1007/s11661-999-0127-4
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Fatigue cracking resistance of sintered steel as a function of temperature is characterized by crack growth rate Its the stress intensity range, Delta K. The stress ratio effects on fatigue crack propagation (FCP) are investigated from room temperature to 300 degrees C. The crack closure effects on FCP are evaluated by both theoretical and experimental approaches. We found that the crack closure cannot be fully responsible for the observed increase of fatigue resistance with low stress ratio. Experimental results support that both K-max and Delta K control near-threshold crack growth. Fatigue crack resistance at high Delta K regime decreases with temperature. The apparent increase of fatigue resistance at the near-threshold regime at elevated temperatures might be attributed to microcrack toughening.
引用
收藏
页码：2895 / 2904
页数：10
相关论文
共 50 条
  • [21] Fatigue behavior and fracture of sintered
    Sotelo, GFC
    Brand, U
    ADVANCED POWDER TECHNOLOGY, 1999, 299-3 : 330 - 337
  • [22] Fatigue life and fatigue crack propagation behavior of JLF-1 steel
    Yoon, HK
    Lee, SP
    Min, BH
    Kim, SW
    Katoh, Y
    Kohyama, A
    FUSION ENGINEERING AND DESIGN, 2002, 61-62 : 677 - 682
  • [23] Fatigue crack propagation behavior of Ni-based superalloys after overloading at elevated temperatures
    Xinyue Huang
    Liang Wang
    Yunming Hu
    Guangping Guo
    David Salmon
    Ying Li
    Wenxia Zhao
    Progress in Natural Science:Materials International, 2016, 26 (02) : 197 - 203
  • [24] Fracture mechanics and fatigue crack propagation in armor steel welds
    Cabrilo, Aleksandar
    Sedmak, Aleksandar
    Burzic, Zijah
    Perkovic, Srdja
    ENGINEERING FAILURE ANALYSIS, 2019, 106
  • [25] Fatigue crack propagation behavior of Ni-based superalloys after overloading at elevated temperatures
    Huang, Xinyue
    Wang, Liang
    Hu, Yunming
    Guo, Guangping
    Salmon, David
    Li, Ying
    Zhao, Wenxia
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2016, 26 (02) : 197 - 203
  • [26] FATIGUE CRACK GROWTH AND THRESHOLD BEHAVIOR AT ELEVATED TEMPERATURES.
    Ogura, Keiji
    Miyoshi, Yoshio
    Nishikawa, Izuru
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (473): : 89 - 98
  • [27] FATIGUE BEHAVIOR OF SINTERED STEEL
    HAGER, B
    POHLANDT, K
    STAHL UND EISEN, 1991, 111 (09): : 129 - 134
  • [28] Fatigue crack propagation behaviour of a nickel based superalloy at elevated temperatures
    Wang, L.
    Huang, X.
    Guo, G.
    Hu, Y.
    Zhang, L.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 1087 - 1090
  • [29] FATIGUE CRACK-PROPAGATION IN LIQUID LITHIUM AT ELEVATED-TEMPERATURES
    HAMMON, DL
    OLSON, DL
    MATLOCK, DK
    JOURNAL OF METALS, 1979, 31 (12): : 87 - 87
  • [30] Quantitative models on corrosion fatigue crack growth rates in metals: Part II. application of fatigue crack growth rate modeling for nickel-based superalloys at elevated temperatures
    Sang Shik Kim
    Seung Joo Choe
    Kwang Seon Shin
    Metals and Materials, 1998, 4 : 15 - 23
12345