Microstructure and electrochemical properties of nanostructured WC-10Co-4Cr coating prepared by HVOF spraying

被引：48

作者：

Hong, Sheng ^{[1
]}

Wu, Yuping ^{[1
]}

Zheng, Yugui ^{[2
]}

Wang, Bo ^{[1
]}

Gao, Wenwen ^{[1
]}

Lin, Jinran ^{[1
]}

机构：

[1] Hohai Univ, Coll Mech & Mat, Inst Met & Protect, Nanjing 210098, Jiangsu, Peoples R China

[2] Chinese Acad Sci, Inst Met Res, State Key Lab Corros & Protect, Shenyang 110016, Peoples R China

来源：

SURFACE & COATINGS TECHNOLOGY | 2013年 / 235卷

关键词：

HVOF; Nanostructured; WC-Co-Cr coating; Microstructure; Corrosion; STRONG ACIDIC ENVIRONMENT; IMPEDANCE PLANE DISPLAYS; SILT EROSION BEHAVIOR; WC-COCR COATINGS; HARD CHROMIUM; CORROSION BEHAVIOR; MECHANICAL-PROPERTIES; STABILITY CONDITIONS; METALLIC-GLASS; STEADY-STATE;

D O I：

10.1016/j.surfcoat.2013.08.029

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A nanostructured WC-10Co-4Cr coating was deposited on the substrate of AISI 1045 steel by means of high-velocity oxygen-fuel (HVOF) thermal spraying process. The detailed microstructures and phase composition of the coating were analyzed by using X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), differential scanning calorimeter (DSC) and high-resolution transmission electron microscope (HRTEM). It was revealed that the amorphous phase, nanoclusters and carbides, including W2C and WC were present in the coating. The coating with low porosity of 0.85% had a dense structure and good thermostability. The temperature of the amorphous phase transforming into the nanocrystalline structure was 645 degrees C. Corrosion behavior of the coatings was investigated by electrochemical measurement. The results showed that the coating exhibited better corrosion resistance than the hard chromium coating in 3.5 wt.% NaCl solution. (C) 2013 Elsevier B.V. All rights reserved.

引用

页码：582 / 588

页数：7

共 50 条

[31] Effect of abrasive particle size on friction and wear behaviour of HVOF sprayed WC-10Co-4Cr coating
Sahariah, Bikram Jyoti
Vashishtha, Nitesh
Sapate, S. G.
MATERIALS RESEARCH EXPRESS, 2018, 5 (06):
[32] Tribological Behavior of Cermet Coatings Deposited from Submicron WC-10Co-4Cr Powders Using HVOF Spraying
Hong, Sheng
Wu, Yuping
Wang, Bo
MATERIALS SCIENCE-MEDZIAGOTYRA, 2019, 25 (03): : 303 - 308
[33] Effect of Coating Thickness on the Slurry Erosion Resistance of HVOF-Sprayed WC-10Co-4Cr Coatings
S. G. Sapate
N. Tangselwar
S. N. Paul
R. C. Rathod
Sanket Mehar
D. S. Gowtam
Manish Roy
Journal of Thermal Spray Technology, 2021, 30 : 1365 - 1379
[34] Microstructure and Properties of the Cermet Coating Prepared by Spraying Multimodal WC-17Co Powders Using HVOF Technique
Chen X.
Bai X.
Wang H.
Ji G.
Cailiao Daobao/Materials Reports, 2019, 33 (02): : 684 - 688
[35] HVOF process optimization for the erosion resistance of WC-12Co and WC-10Co-4Cr coatings
Arsenault, B
Legoux, JG
Hawthorne, H
Immarigeon, JP
Gougeon, P
Moreau, C
THERMAL SPRAY 2001: NEW SURFACES FOR A NEW MILLENNIUM, 2001, : 1051 - 1060
[36] HVOF喷涂WC-10Co-4Cr涂层耐泥沙冲蚀研究
王华仁
张光华
李曙
刘阳
东方电气评论, 2011, 25 (01) : 41 - 47
[37] HVOF和APS喷涂WC-10Co-4Cr涂层性能研究
陈焕涛
陈文龙
张晓锋
黄健
张忠诚
朱晖朝
黄仁忠
黄科
叶云
朱霞高
陈志坤
黄科里
王子乐
陈江
周广鑫
材料研究与应用, 2017, 11 (01) : 30 - 33
[38] HVOF喷涂WC-10Co-4Cr涂层的砂浆冲蚀行为
张光华
李曙
刘阳
王华仁
中国表面工程, 2007, (04) : 16 - 22+28
[39] Cavitation Erosion Behavior and Mechanism of HVOF Sprayed WC-10Co-4Cr Coating in 3.5 wt% NaCl Solution
Hong, Sheng
Wu, Yuping
Zhang, Jianfeng
Zheng, Yugui
Qin, Yujiao
Gao, Wenwen
Li, Gaiye
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2015, 68 (01) : 151 - 159
[40] Experimental Investigation of Ultrasonic Vibration-Assisted Grinding of HVOF-Sprayed WC-10Co-4Cr Coating
Ji, Ning
Zhang, Junhong
Liu, Minjie
Dai, Huwei
Ding, Kunying
Yu, Jun
Zhang, Xueling
COATINGS, 2023, 13 (10)

← 1 2 3 4 5 →