Ferroelectric properties of modified lead titanate thin films obtained by a sol-gel method

Calcium substituted lead titanate thin films have been prepared by a sol-gel method, deposited by spin-coating, and thermally treated so as to obtain a perovskite structure. Two types of thermal treatments were given, differing in the heating rate, which in conventional treatments was of some 10 degrees C/min, and in rapid treatments >500 degrees C/min. With rapid heating, materials are obtained in which greater polarizations are commuted and bias fields are smaller. This, together with the fact that additional (undesired) phases are not observed by X-ray diffractometry when rapid treatments are used, shows that these are to be preferred over conventional treatments.