A composite material with CeO2-ZrO2 nanocrystallines embedded in SiO2 matrices and its enhanced thermal stability and oxygen storage capacity

被引：3

作者：

Yang, Runnong ^{[1
]}

Liu, Yumei ^{[1
,2
]}

Yu, Lin ^{[1
]}

Zhao, Xiangyun ^{[2
]}

Yang, Xiaobo ^{[1
,2
]}

Sun, Ming ^{[1
]}

Luo, Junyin ^{[1
]}

Fan, Qun ^{[1
,2
]}

Xiao, Jianming ^{[2
]}

Zhao, Yuzhong ^{[2
]}

机构：

[1] Guangdong Univ Technol, Sch Chem Engn & Light Ind, Key Lab Clean Chem Technol Guangdong Regular High, Guangzhou 510006, Guangdong, Peoples R China

[2] Waygreen Technol Inc, Guangzhou 511441, Guangdong, Peoples R China

来源：

JOURNAL OF NANOPARTICLE RESEARCH | 2018年 / 20卷 / 06期

基金：

中国国家自然科学基金;

关键词：

Ceria-zirconia nanocrystallites; Silica matrices; Thermal stability; Oxygen storage capacity; Three-way catalyst; CEO2-ZRO2 MIXED OXIDES; CERIA-ZIRCONIA; CO OXIDATION; SILICA; NANOPARTICLES; CATALYSTS; SUPPORTS; ALUMINA; PERFORMANCE; REDUCTION;

D O I：

10.1007/s11051-018-4255-x

中图分类号：

O6 [化学];

学科分类号：

0703 ;

摘要：

A simple hydrothermal procedure is introduced, which leads to the successful synthesis of a new composite material with fine CeO2-ZrO2 nanocrystallites embedded in amorphous and porous SiO2 matrices. The composite material possesses an extraordinary high thermal stability. After being calcined at 1000 \s=deg\C, it retains CeO2-ZrO2 nanocrystallites of the size around 5 nm, a BET-specific surface area of 165 m(2)/g, and an oxygen storage capacity of 468 \g=m\mol/g. No phase segregation for CeO2-ZrO2 nanocrystallites is detected and the SiO2 matrices remain not crystallized. The composite material shows a great potential as a support of three-way catalyst, as evidenced in catalytic tests with supported Pt.

引用

页数：13

共 50 条

[21] Nanosized CeO2–SiO2, CeO2–TiO2, and CeO2–ZrO2 Mixed Oxides: Influence of Supporting Oxide on Thermal Stability and Oxygen Storage Properties of Ceria
Benjaram M. Reddy
Ataullah Khan
Catalysis Surveys from Asia, 2005, 9 : 155 - 171
[22] Oxygen buffering capacity of Pr/Tb doped CeO2-ZrO2 mixed oxides
Fan, Guo-Dong
Zhang, Zhao
Feng, Chang-Gen
Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2008, 18 (09): : 1742 - 1747
[23] Single-phase PrOy-ZrO2 materials and their oxygen storage capacity:: A comparison with single-phase CeO2-ZrO2, PrOy-CeO2, and PrOy-CeO2-ZrO2 materials
Narula, CK
Haack, LP
Chun, W
Jen, HW
Graham, GW
JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (18): : 3634 - 3639
[24] Enhancement of oxygen storage capacity by reductive treatment of Al2O3 and CeO2-ZrO2 solid solution nanocomposite
Morikawa, Akira
Kikuta, Koichi
Suda, Akihiko
Shinjo, Hirofumi
APPLIED CATALYSIS B-ENVIRONMENTAL, 2009, 88 (3-4) : 542 - 549
[25] Role of CeO2-ZrO2 in diesel soot oxidation and thermal stability of potassium catalyst
Wu, Xiaodong
Liu, Dongxu
Li, Kai
Li, Jia
Weng, Duan
CATALYSIS COMMUNICATIONS, 2007, 8 (08) : 1274 - 1278
[26] Role of Surface Adsorption in Fast Oxygen Storage/Release of CeO2-ZrO2 Mixed Oxides
吴晓东
梁清
吴筱笛
翁端
Journal of Rare Earths, 2007, (04) : 416 - 421
[27] Encapsulating Ni/CeO2-ZrO2 with SiO2 layer to improve it catalytic activity for steam reforming of toluene
Zhao, Xiaoyong
Xue, Yaping
Lu, Zhuoxin
Huang, Ying
Guo, Changqing
Yan, Changfeng
CATALYSIS COMMUNICATIONS, 2017, 101 : 138 - 141
[28] Role of surface adsoption in fast oxygen Storage/Release of CeO2-ZrO2 mixed oxides
Wu, Xiaodong
Qing, Liang
Wu, Xiaodi
Duan, Weng
JOURNAL OF RARE EARTHS, 2007, 25 (04) : 416 - 421
[29] Transient analysis of oxygen storage capacity of Pt/CeO2-ZrO2 materials with millisecond- and second-time resolution
Kondratenko, Evgenii V.
Sakamoto, Yoshiyuki
Okumura, Kohei
Shinjoh, Hirofumi
APPLIED CATALYSIS B-ENVIRONMENTAL, 2009, 89 (3-4) : 476 - 483
[30] Effect of SiO2 on the thermal stability of carbonate/MgO composite for thermal energy storage
Guo, Y. R.
Liu, Y.
Zhang, G. Q.
Deng, Z. F.
Xu, G. Z.
Li, B. R.
2ND INTERNATIONAL WORKSHOP ON MATERIALS SCIENCE AND MECHANICAL ENGINEERING (IWMSME2018), 2019, 504

← 1 2 3 4 5 →