Crack initiation on 316L(N) CT specimens under creep-fatigue conditions

被引：0
|
作者：
Laiarinandrasana, L [1 ]
Piques, R [1 ]
Drubay, B [1 ]
Faidy, C [1 ]
机构：
[1] URA CNRS 866, EMP, F-91003 Evry, France
来源：
LIFE ASSESSMENT AND LIFE EXTENSION OF ENGINEERING PLANT, STRUCTURES AND COMPONENTS | 1996年
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In power plant operating at elevated temperatures, components are subjected to complex loading history including creep, fatigue and creep-fatigue effects. A practical and validated method for calculating the initiation time for pre-existing defects is needed. An attempt is made to analyze creep-fatigue tests performed at both the Ecole des Mines de Paris (EMP) and the Commissariat a l'Energie Atomique (CEA) Saclay on 316L(N) CT specimens, by combining local and global approaches on crack initiation with Fracture Mechanics concepts.
引用
收藏
页码：95 / 102
页数：8
相关论文
共 50 条
  • [31] FATIGUE CRACK GROWTH IN 316L UNDER UNIAXIAL AND TORSIONAL LOADING
    Karol', Michal
    Chlupova, Alice
    Mazanova, Veronika
    Kruml, Tomas
    METAL 2016: 25TH ANNIVERSARY INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2016, : 568 - 573
  • [32] Creep-fatigue initiation and early crack growth in Inconel 718
    Reed, PAS
    Hachette, F
    Thakar, D
    Connolley, T
    Starink, MJ
    PROGRESS IN MECHANICAL BEHAVIOUR OF MATERIALS (ICM8), VOL 1: FATIGUE AND FRACTURE, 1999, : 418 - 423
  • [33] CHARACTERIZATION OF LOW-CYCLE FATIGUE AND CREEP-FATIGUE INDUCED DAMAGE IN A 316L STAINLESS-STEEL
    SIMON, S
    IBABE, JMR
    FUENTES, M
    ZEITSCHRIFT FUR METALLKUNDE, 1994, 85 (04): : 273 - 281
  • [34] CHARACTERIZATION FOR CRACK INITIATION LIFE, PROPAGATION LIFE AND TOTAL FRACTURE LIFE, RESPECTIVELY UNDER HIGH TEMPERATURE CREEP, FATIGUE AND CREEP-FATIGUE CONDITIONS.
    Yokobori, Toshimitsu
    Yokobori, Takeo
    Kuriyama, Takashi
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1986, 52 (477): : 1215 - 1220
  • [35] Crack-growth behavior of alloy 230 under creep-fatigue conditions
    Roy, A. K.
    Chatterjee, S.
    Hasan, M. H.
    Pal, J.
    Ma, L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (18-19): : 4830 - 4836
  • [36] An idea for predicting crack growth time to fracture under creep-fatigue conditions
    Geng, MF
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1998, 257 (02): : 250 - 255
  • [37] Idea for predicting crack growth time to fracture under creep-fatigue conditions
    Geng, Ming-Fa
    Materials Science and Engineering A, 1998, 257 (02): : 250 - 255
  • [38] Crack growth morphology and microstructural changes in 316 stainless steel under creep-fatigue cycling
    Gao, N.
    Brown, M.W.
    Miller, K.J.
    Fatigue and Fracture of Engineering Materials and Structures, 1995, 18 (12): : 1407 - 1422
  • [39] Crack growth morphology and microstructural changes in 316 stainless steel under creep-fatigue cycling
    Gao, N
    Brown, MW
    Miller, KJ
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (12) : 1407 - 1421
  • [40] Crack growth behaviour of P92 steel under creep and creep-fatigue conditions
    Shi, K. X.
    Lin, F. S.
    Wan, H. B.
    Wang, Y. F.
    MATERIALS AT HIGH TEMPERATURES, 2014, 31 (04) : 343 - 347
12345