The Effect of RRA Heat Treatment on the Intergranular Corrosion (IGC) of the AA7075 Alloy

被引：6
|
作者：
Ozer, G. [1 ]
Karaaslan, A. [1 ]
机构：
[1] Yildiz Tech Univ, Dept Met & Mat Engn, Davutpasa Campus, TR-34210 Istanbul, Turkey
来源：
PRAKTISCHE METALLOGRAPHIE-PRACTICAL METALLOGRAPHY | 2017年 / 54卷 / 04期
关键词：
ZN-MG ALLOY;
D O I：
10.3139/147.110453
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
In this study, the effects of retrogression and re-aging (RRA) heat treatment applied on AA7075 aluminum alloy at various times and temperatures on the intergranular corrosion (IGC) behavior were investigated. The IGC solution was prepared according to ASTM G110-92 standard and the samples were kept in the solution for 24 hours. Susceptibility of the alloy to IGC was determined by weight loss detection, macro and microstructure studies. Scanning electron microscope (SEM) analysis was also performed. According to the results obtained, it was determined that the RRA processes in the AA7075 alloy change the grain boundary morphology and decrease the IGC corrosion susceptibility.
引用
收藏
页码：256 / 266
页数：11
相关论文
共 50 条
  • [21] Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy
    Marunkic, Dunja
    Pejic, Jovanka
    Jegdic, Bore
    Marinkovic, Aleksandar
    Radojkovic, Bojana
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (06): : 950 - 960
  • [22] Galvanic compatibility of corrosion protective coatings with AA7075 aluminum alloy
    Lodhi, Z. F.
    Hamer, W. J.
    Mol, J. M. C.
    Terryn, H.
    de Wit, J. H. W.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2008, 59 (04): : 306 - 310
  • [23] Evolution of corrosion behavior for AA7075 aluminum alloy implanted with nitrogen
    Abreu, C. M.
    Cristobal, M. J.
    Figueroa, R.
    Novoa, X. R.
    Pena, G.
    NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS, 2019, 442 : 1 - 12
  • [24] Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy
    Marunkić, Dunja
    Pejić, Jovanka
    Jegdić, Bore
    Marinković, Aleksandar
    Radojković, Bojana
    Materials and Corrosion, 2022, 73 (06) : 950 - 960
  • [25] Effect of Thermomechanical Treatment on the Environmentally Induced Cracking Behavior of AA7075 Alloy
    Rahul Ghosh
    A. Venugopal
    P. Sankaravelayudham
    Rajiv Panda
    S. C. Sharma
    Koshy M. George
    V. S. Raja
    Journal of Materials Engineering and Performance, 2015, 24 : 545 - 555
  • [26] Metallurgical and corrosion characteristics of AA7075 alloy reinforced with Nickel foam
    Karthik, Sadhu
    Krishna, Kothapelli Varun
    Anirudha, D.
    Vignesh, S.
    Vaira Vignesh, R.
    COMPOSITE INTERFACES, 2024, 31 (06) : 701 - 727
  • [27] Effect of Thermomechanical Treatment on the Environmentally Induced Cracking Behavior of AA7075 Alloy
    Ghosh, Rahul
    Venugopal, A.
    Sankaravelayudham, P.
    Panda, Rajiv
    Sharma, S. C.
    George, Koshy M.
    Raja, V. S.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2015, 24 (02) : 545 - 555
  • [28] Effect of scandium addition on the erosion corrosion behaviour of AA7075
    Department of Mechanical Engineering, Tagore Engineering College, Chennai, India
    J. Corros. Sci. Eng., 2015
  • [29] Microstructure, mechanical and corrosion behavior of high strength AA7075 aluminium alloy friction stir welds - Effect of post weld heat treatment
    Kumar, P. Vijaya
    Reddy, G. Madhusudhan
    Rao, K. Srinivasa
    DEFENCE TECHNOLOGY, 2015, 11 (04): : 362 - 369
  • [30] The effect of chloride concentration and pH on pitting corrosion of AA7075 aluminum alloy coated with phenyltrimethoxysilane
    A. A. Younis
    M. M. B. El-Sabbah
    Rudolf Holze
    Journal of Solid State Electrochemistry, 2012, 16 : 1033 - 1040
12345