On the fracture behavior of uranium subjected to shock-wave loading in the temperature range -196 to 800 degrees C

被引：0
|
作者：
Golubev, VK
Sobolev, YS
Yukina, NA
机构：
来源：
RUSSIAN METALLURGY | 1997年 / 02期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The spall-type fracture of uranium was investigated in the temperature range -196 to 800 degrees C. The critical levels of shock-wave loading were determined, responsible for the initiation of the spall sites and complete macroscopic failure of the specimens. The data are described of metallographic research into the fracture behavior of uranium at various test temperatures.
引用
收藏
页码：103 / 105
页数：3
相关论文
共 50 条
  • [11] TEMPERATURE CONDUCTIVITY OF A URANIUM OXIDE-SILICON OXIDE SYSTEM WITH DIFFERENT URANIUM DIOXIDE CONCENTRATIONS IN A TEMPERATURE RANGE BETWEEN 100 DEGREES-C AND 800 DEGREES-C
    GLANZ, G
    JOURNAL OF NUCLEAR MATERIALS, 1969, 29 (03) : 329 - &
  • [12] Some new data on deformation and fracture of solids under shock-wave loading
    Kanel, GI
    JOURNAL OF THE MECHANICS AND PHYSICS OF SOLIDS, 1998, 46 (10) : 1869 - 1886
  • [13] Shock-Wave Loading and Spall Fracture of Textured Tungsten Samples: Experiment and Simulation
    A. M. Molodets
    A. S. Savinykh
    A. A. Golyshev
    G. V. Garkushin
    G. V. Shilov
    A. N. Nekrasov
    Physics of Metals and Metallography, 2022, 123 : 520 - 527
  • [14] Shock-Wave Loading and Spall Fracture of Textured Tungsten Samples: Experiment and Simulation
    Molodets, A. M.
    Savinykh, A. S.
    Golyshev, A. A.
    Garkushin, G., V
    Shilov, G., V
    Nekrasov, A. N.
    PHYSICS OF METALS AND METALLOGRAPHY, 2022, 123 (05): : 520 - 527
  • [15] CHARACTER OF SPALLING FAILURE OF COPPER, NICKEL, TITANIUM, AND IRON IN THE -196-DEGREES-C TO 800-DEGREES-C RANGE
    GOLUBEV, VK
    NOVIKOV, SA
    SOBOLEV, YS
    YUKINA, NA
    STRENGTH OF MATERIALS, 1983, 15 (03) : 390 - 396
  • [16] MEASUREMENT OF MAGNETOSTRICTION WITHIN THE TEMPERATURE RANGE -196-DEGREES-C TO 400-DEGREES-C
    BIRSS, RR
    LEE, EW
    JOURNAL OF SCIENTIFIC INSTRUMENTS, 1960, 37 (07): : 225 - 230
  • [17] Behavior of 40Ar in obsidian subjected to strong shock-wave compression
    Badyukov, DD
    Kozlov, EA
    Kolesnikov, EM
    Lebedeva, LM
    Nazarov, MA
    DOKLADY EARTH SCIENCES, 2000, 373 (05) : 905 - 907
  • [18] Effect of carbide precipitation on the creep behavior of alloy 800HT in the temperature range 700 degrees C to 900 degrees C
    ElMagd, E
    Nicolini, G
    Farag, M
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (03): : 747 - 756
  • [19] Deformation and fracture characteristics in TiAl at room temperature and 800 degrees C
    Wiezorek, JMK
    Mills, MJ
    Fraser, HL
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 234 : 1106 - 1109
  • [20] OXIDATION OF TITANIUM IN THE TEMPERATURE RANGE 800-1200-DEGREES-C
    KOFSTAD, P
    ANDERSON, PB
    KRUDTAA, OJ
    JOURNAL OF THE LESS-COMMON METALS, 1961, 3 (02): : 89 - 97
12345