Corrosion behavior of 2099 Al-Li alloy in NaCl aqueous solution

被引：12
|
作者：
Chen, Bin [1 ]
Li, Chao-Hao [1 ]
He, Shi-Chen [1 ]
Li, Xiao-ling [1 ]
Lu, Chen [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai 200240, Peoples R China
来源：
JOURNAL OF MATERIALS RESEARCH | 2014年 / 29卷 / 12期
关键词：
CU-MG ALLOYS; PITTING CORROSION; ELECTROCHEMICAL-BEHAVIOR; ALUMINUM-ALLOY; AEROSPACE; FILMS;
D O I：
10.1557/jmr.2014.121
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion behavior of 2099 Al-Li alloy in NaCl aqueous solutions with different concentrations (1.5, 3.5, and 5.0% in mass fraction) was investigated. Its corrosion resistance was evaluated using electrochemical measurements together with full immersion tests. The results showed that the 2099 Al-Li alloy possessed good corrosion resistance in NaCl aqueous solutions. Its corrosion rate increased with increasing chloride ion concentration. The main form of corrosion failure was pitting corrosion. The impurity containing sulfur leads to surface pitting. The oxide films that formed during the manufacturing process offer a good resistance to corrosion. They are likely to suffer separation, cracking, and drop-off when immersed in aggressive NaCl aqueous solution. The good corrosion susceptibility of the alloy may be attributed to homogeneous coherent nanoscale precipitates.
引用
收藏
页码：1344 / 1353
页数：10
相关论文
共 50 条
  • [31] Stress-corrosion cracking characterisation of the advanced aerospace Al-Li 2099-T86 alloy
    Goebel, J.
    Ghidini, T.
    Graham, A. J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 673 : 16 - 23
  • [32] Homogenization process of 2099 Al-Li alloys
    Zheng, Z. (s-maloy@mail.csu.edu.cn), 1600, Central South University of Technology (44):
  • [33] Fatigue Crack Growth of Al-Li Alloy 2091 in 3.5% NaCl Solution and at 130℃
    何世禹
    王中光
    李清建
    张匀
    冯晓曾
    Journal of Materials Science & Technology, 1992, (05) : 359 - 364
  • [34] Exfoliation corrosion and electrochemical impedance spectroscopy of an Al-Li alloy in EXCO solution
    Li, J. F.
    Zheng, Z. Q.
    Li, S. C.
    Ren, W. D.
    Chen, W. J.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2007, 58 (04): : 273 - 279
  • [35] The passive film characteristics of several plastic deformation 2099 Al-Li alloy
    Lv Jinlong
    Liang Tongxiang
    Wang Chen
    Guo Ting
    JOURNAL OF ALLOYS AND COMPOUNDS, 2016, 662 : 143 - 149
  • [36] Corrosion behavior of Mg-Y alloy in NaCl aqueous solution
    Xin Zhang a
    Progress in Natural Science:Materials International, 2012, 22 (02) : 169 - 174
  • [37] Corrosion behavior of Mg-Y alloy in NaCl aqueous solution
    Zhang, Xin
    Zhang, Kui
    Deng, Xia
    Li, Hongwei
    Li, Yongjun
    Ma, Minglong
    Li, Ning
    Wang, Yanlong
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2012, 22 (02) : 169 - 174
  • [38] Influence of aging treatment on corrosion behavior of extruded 2195 Al-Li alloy
    Li, Hui
    Wang, Zhi-wen
    Fu, Rong
    Huang, Yuan-chun
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2024, 34 (03) : 755 - 768
  • [39] Multiaxial fatigue behavior and life estimation of Al-Li alloy 2099 under strain-controlled loading
    Merah, Nesar
    Albinmousa, Jafar
    Adinoyi, Muhammed J.
    Ali, Usman
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, 47 (10) : 3757 - 3772
  • [40] Analysis of Low-Cycle Fatigue Behavior of AW2099-T83 Al-Li Alloy
    Adinoyi, Muhammed J.
    Merah, Necar
    Albinmousa, Jafar
    FRATTURA ED INTEGRITA STRUTTURALE, 2019, 13 (49): : 487 - 506
12345