Determining fracture toughness from cutting tests on polymers

被引:65
|
作者
Patel, Y. [1 ]
Blackman, B. R. K. [1 ]
Williams, J. G. [1 ,2 ]
机构
[1] Univ London Imperial Coll Sci Technol & Med, Dept Mech Engn, London SW7 2AZ, England
[2] Univ Sydney, Aero Mech & Mechatron Engn Dept, Sydney, NSW 2006, Australia
关键词
Cutting; Fracture toughness; Adhesion; Friction; Shear;
D O I
10.1016/j.engfracmech.2009.07.019
中图分类号
O3 [力学];
学科分类号
08 ; 0801 ;
摘要
A cutting test method has been developed for polymers and analysis schemes derived for the determination of the fracture toughness, G(c) from the cutting data. The experimental scheme requires the measurement of forces for a cut of width b, in both the cutting direction, F-c/b and the transverse direction, F-t/b. Depths of cut were varied from 0.025 mm to 0.25 mm and the tool rake angle was varied from -20 degrees to 30 degrees. Cutting was performed at a speed of 10 mm s(-1) on three polymers (HIPS, PA 4/6 and LLDPE). In addition, values of fracture toughness and yield strength were determined for the polymers using standard tests for comparison with the values obtained from cutting. Three analysis methods were derived to analyse the cutting data with the most favoured scheme based on an energy balance and using Merchant's force minimisation criterion to determine the shear plane angle. This avoids the need to measure the cut chip thickness. Results for HIPS and PA 4/6 gave values of G(c) in good agreement with the values determined via LEFM. However, the cutting method is intended for materials such as LLDPE which has a low yield stress and moderately high toughness, i.e. materials which cannot be tested using standard LEFM fracture mechanics tests. The cutting analysis appeared to give valid values of G(c) for LLDPE in that they were independent of rake angle. There were some complications when analysing this polymer due to visco-elastic recovery effects in the chip and these have been considered. Finally, the cutting analyses always determined high values of yield stress which would appear to indicate work hardening. (C) 2009 Elsevier Ltd. All rights reserved.
引用
收藏
页码:2711 / 2730
页数:20
相关论文
共 50 条
  • [31] PREDICTION OF VARIATION IN FRACTURE TOUGHNESS FROM SMALL SPECIMEN TESTS.
    Tetelman, A.S.
    Wullaert, R.A.
    Ireland, D.
    1971, : 85 - 92
  • [32] METHOD OF EXTRACTING DYNAMIC FRACTURE-TOUGHNESS FROM CT TESTS
    GEHLEN, PC
    HOAGLAND, RG
    POPELAR, CH
    INTERNATIONAL JOURNAL OF FRACTURE, 1979, 15 (01) : 69 - 84
  • [33] Fracture toughness values obtained from tensile tests on unnotched specimens
    Schmelzer, Peter
    Schneeweiss, Guenther
    Varga, Thomas
    Materialpruefung/Materials Testing, 1998, 40 (1-2): : 34 - 38
  • [34] FRACTURE-TOUGHNESS TESTING OF TOUGHENED POLYMERS
    HUANG, DD
    ADVANCES IN CHEMISTRY SERIES, 1993, (233): : 39 - 59
  • [35] TOOL FAILURE BY FRACTURE AND FRACTURE-TOUGHNESS OF CUTTING TOOL MATERIALS
    RAMALINGAM, S
    JOURNAL OF METALS, 1979, 31 (08): : F32 - F32
  • [36] EFFECT OF TEMPERATURE ON IMPACT FRACTURE TOUGHNESS OF POLYMERS
    PLATI, E
    WILLIAMS, JG
    POLYMER, 1975, 16 (12) : 915 - 920
  • [37] Criteria of ceramics fracture (edge chipping and fracture toughness tests)
    Gogotsi, G. A.
    CERAMICS INTERNATIONAL, 2013, 39 (03) : 3293 - 3300
  • [38] Determining the fracture toughness of quasi-brittle materials with notched four-point bending tests
    Han, Xiangyu
    Xiao, Qinghua
    Cui, Kai
    Hu, Xiaozhi
    Zhou, Zelin
    ENGINEERING FRACTURE MECHANICS, 2023, 284
  • [39] Determining specimen thickness limit in fracture toughness tests applied to dental ceramics and metal alloy interfaces
    Porto, Carla Pereira Santos
    Cardoso, Raphael Calazans
    Pereira, Luiz Carlos
    Griza, Sandro
    Bergmann, Carlos Perez
    CERAMICS INTERNATIONAL, 2022, 48 (01) : 803 - 810
  • [40] FRACTURE TOUGHNESS TESTS OF A RIGID POLYURETHANE FOAM
    FOWLKES, CW
    INTERNATIONAL JOURNAL OF FRACTURE, 1974, 10 (01) : 99 - 108