COMPARISON OF A CYCLIC BEHAVIOR OF 316L STEEL IN UNIAXIAL AND MULTIAXIAL CYCLIC LOADING

被引:0
|
作者
Poczklan, L. [1 ]
Mazanova, V [1 ]
Kruml, T. [2 ]
机构
[1] Inst Phys Mat, Zizkova 22, Brno 61662, Czech Republic
[2] CEITEC IPM, Zizkova 22, Brno 61662, Czech Republic
来源
ENGINEERING MECHANICS 2019 | 2019年 / 25卷
关键词
fatigue behavior; multiaxial cyclic loading; phase transformation; 316L stainless steel; fatigue crack initiation; STAINLESS-STEEL; DISLOCATION-STRUCTURES; FATIGUE;
D O I
10.21495/71-0-287
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
A study of the cyclic behavior of austenitic stainless steel 316L was carried out in uniaxial loading, pure torsional loading and multiaxial in phase loading. Experiments were performed on hollow cylindrical specimens with polished surface. The specimens were cyclically loaded at room temperature with constant total strain amplitude. The specimen surface was observed by scanning electron microscopy and the microstructure was investigated by transmission electron microscopy. Differences in the mechanical response in different loading modes are discussed. It was found that the exhibited secondary hardening is caused by both the phase transformation and the appearance of alpha' martensite. The phase transformation is more intense in the case of torsional loading as compared to axial loading. The crack initiation mechanism does not change considerably in individual modes. Persistent slip bands occur and fatigue cracks initiate along them.
引用
收藏
页码:287 / 290
页数:4
相关论文
共 50 条
  • [21] CYCLIC PLASTICITY IN TYPE 316L AUSTENITIC STAINLESS-STEEL
    POLAK, J
    OBRTLIK, K
    HAJEK, M
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1994, 17 (07) : 773 - 782
  • [22] Constant and variable amplitude cyclic plasticity in 316L stainless steel
    van Eeten, Paul
    Nilsson, Fred
    JOURNAL OF TESTING AND EVALUATION, 2006, 34 (04) : 298 - 311
  • [23] Effect of notches on the deformation behavior and damage evolution of additively manufactured 316L specimens under uniaxial quasi-static and cyclic loading
    Brenne, F.
    Niendorf, T.
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 127 : 175 - 189
  • [24] Crack initiation and propagation of 30CrMnSiA steel under uniaxial and multiaxial cyclic loading
    Liu, Tianqi
    Shi, Xinhong
    Zhang, Jianyu
    Fei, Binjun
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 122 : 240 - 255
  • [25] Dissipative and thermal aspects in cyclic loading of additive manufactured AISI 316L
    Santoro, Luca
    Sesana, Raffaella
    Diller, Johannes
    Radlbeck, Christina
    Mensinger, Martin
    ENGINEERING FAILURE ANALYSIS, 2024, 163
  • [26] Electrochemical Behavior of Type 316L Stainless Steel during Cyclic Deformation under Cell Culturing
    Doi, Kotaro
    Miyabe, Sayaka
    Fujimoto, Shinji
    JOURNAL OF THE JAPAN INSTITUTE OF METALS AND MATERIALS, 2015, 79 (06) : 303 - 307
  • [27] Study on multiaxial low cycle fatigue under nonproportional loading of 316l stainless steel
    Guoqiu, He
    Chengshu, Chen
    Qing, Gao
    Xunfang, Sun
    Zhiyun, Shen
    Jixie Gongcheng Xuebao/Chinese Journal of Mechanical Engineering, 35 (01):
  • [28] Investigation of the anisotropic cyclic damage behavior of selective laser melted AISI 316L stainless steel
    Stern, Felix
    Kleinhorst, Jan
    Tenkamp, Jochen
    Walther, Frank
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2019, 42 (11) : 2422 - 2430
  • [29] Electrochemical Behavior of Type 316L Stainless Steel during Cyclic Deformation under Cell Culturing
    Doi, Kotaro
    Miyabe, Sayaka
    Fujimoto, Shinji
    MATERIALS TRANSACTIONS, 2014, 55 (12) : 1890 - 1894
  • [30] Cyclic deformation and fatigue behavior of 316L stainless steel processed by surface mechanical rolling treatment
    Carneiro, Luiz
    Wang, Xiaogui
    Jiang, Yanyao
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 134