A method for testing pipe steels under the conditions of sulfide stress cracking

被引：0
|
作者：
Astaf'ev, VI [1 ]
Narushev, VM [1 ]
Tetyueva, TV [1 ]
机构：
[1] Samara State Univ, Samara 443086, Russia
来源：
MATERIALS SCIENCE | 1999年 / 35卷 / 04期
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We propose a testing method for the evaluation of the threshold crack resistance K-Issc of pipe steels under the conditions of sulfide stress corrosion cracking. The values of K-Issc are determined for various casing tubes mode of different types of steel after heat treatment.
引用
收藏
页码：587 / 591
页数：5
相关论文
共 50 条
  • [41] Stress corrosion cracking tests of RPV steels under simultaneous BWR coolant and irradiation conditions
    Ruscák, M
    Kysela, J
    Brozová, A
    Erben, O
    Postler, M
    Brümmer, G
    Hoffmann, H
    Ilg, U
    Rühle, W
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 875 - 882
  • [42] Stress corrosion cracking of reactor pressure vessel steels under boiling water reactor conditions
    Heldt, J
    Seifert, HP
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 901 - 909
  • [43] Assimilation of Production Under Casting and Rolling Conditions of Pipe Rolled Product from Steels of the V-N Microalloying System Resistant to Cold and Hydrogen Sulfide Cracking
    Naumenko, V. V.
    Bagmet, O. A.
    Mursenkov, E. S.
    METALLURGIST, 2019, 63 (1-2) : 163 - 175
  • [44] STRESS CORROSION CRACKING OF HIGH STRENGTH STEELS - TESTING METHODS
    DESANTIS, R
    METALLURGIA ITALIANA, 1970, 62 (12): : 461 - &
  • [45] THE USE OF FRACTURE-MECHANICS IN SULFIDE STRESS CRACKING TESTING
    CHRISTENSEN, C
    HILL, RT
    CORROSION SCIENCE, 1987, 27 (10-11) : 1137 - &
  • [46] Sulfide cracking of structural steels and alloys
    R. K. Melekhov
    L. M. Karvat'skyi
    O. L. Radkevych
    H. M. Krutsan
    O. O. Krokhmal'nyi
    Materials Science, 1998, 34 : 90 - 96
  • [47] EVALUATION OF THE PROTECTIVE EFFECT OF INHIBITORS OF CORROSION, HYDROGEN CHARGING, AND SULFIDE CRACKING OF LINE PIPE STEELS
    ENIKEEV, EK
    GETMANSKII, MD
    MELEKHOV, RK
    KRUTSAN, AM
    SOVIET MATERIALS SCIENCE, 1991, 27 (04): : 353 - 360
  • [48] Sulfide cracking of structural steels and alloys
    Melekhov, RK
    Karvats'kyi, LM
    Radkevych, OI
    Krutsan, HM
    Krokhmal'nyi, OO
    MATERIALS SCIENCE, 1998, 34 (01) : 90 - 96
  • [49] Mechanism of hydro sulfide cracking of steels
    Kushnarenko, V.M.
    Masyuto, O.M.
    Metallovedenie i Termicheskaya Obrabotka Metallov, 1993, (02): : 5 - 8
  • [50] Improvement of Low-Alloy Pipe Steel Sulfide Stress Cracking Resistance
    A. A. Kholodnyi
    Ya. S. Kuznechenko
    Yu. I. Matrosov
    M. V. Il’ichev
    D. I. Yusupov
    Metallurgist, 2019, 63 : 376 - 387
12345