Corrosion behavior of copper in extremely harsh marine atmosphere in Nansha Islands, China

The corrosion behavior of pure copper exposed to the atmosphere of Nansha Islands for 21 months was studied by mass loss method, composition analysis, morphology observation and electrochemical measurements. The results showed that the average corrosion rate of copper exposed for one year was approximately 7.85 mu m/a, implying that Nansha Islands was classified as a corrosion category of CX. The structure and properties of the corrosion product layer generated on the front and back sides of the exposed sample differed significantly. The inner corrosion product layer (Cu2O) on the front side was relatively thick and dense, whereas the outer product layer (Cu2Cl(OH)(3)) was extremely thin. However, the outer product layer on the back side was thicker than the inner layer. Electrochemical measurements indicated that the protection afforded by the corrosion product layer on the front side was improved gradually, while that on the back side was deteriorated.