Dielectric Properties of Paraelectric Ba1-xSrxTiO3 Ceramics

Ba1-xSrxTiO3 solid solutions with x = 0.4, 0.5, 0.6 and 0.75 were prepared by solid state reaction at 1260 degrees C. The complex dielectric constant dispersion was investigated in the frequency range 1Hz divided by 10 MHz for temperatures between -100 degrees C and 100 degrees C. Microwave measurements, performed at room temperature, show amonotonically decrease of the permittivity from about 3000 to 300 with the increase of the strontium content. Moreover, the variation of the dielectric loss from 0.8% to less than 0.2% with the increase with x was observed. The results indicate that the paraelectric Ba1-xSrxTiO3 materials are suitable for microwave applications.